Busca avançada
Ano de início
Entree
(Referência obtida automaticamente do Web of Science, por meio da informação sobre o financiamento pela FAPESP e o número do processo correspondente, incluída na publicação pelos autores.)

Three-dimensional profilometric assessment of Er:YAG laser irradiated unsintered zirconia

Texto completo
Autor(es):
Ferreira da Silva, Beatriz Togoro [1] ; Cesar, Paulo Francisco [2] ; de Freitas, Patricia Moreira [1] ; Palma-Dibb, Regina Guenka [3] ; Matos, Adriana Bona [1]
Número total de Autores: 5
Afiliação do(s) autor(es):
[1] Univ Sao Paulo, Sch Dent, Dept Operat Dent, Av Prof Lineu Prestes, 2227, Cidade Univ, BR-05508000 Sao Paulo, SP - Brazil
[2] Univ Sao Paulo, Sch Dent, Biomat & Oral Biol Dept, Av Prof Lineu Prestes, 2227, Cidade Univ, BR-05508000 Sao Paulo, SP - Brazil
[3] Univ Sao Paulo, Ribeirao Preto Dent Sch, Dept Restorat Dent, Ave Cafe S-N, BR-14040904 Sao Paulo, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: Journal of Materials Science; v. 51, n. 15, p. 7266-7275, AUG 2016.
Citações Web of Science: 0
Resumo

This study evaluated the effects of different Er:YAG laser pulse width protocols on surface roughness, loss of volume of the material, and the step height formed of pre-sintered yttrium-stabilized tetragonal zirconia polycrystalline (Y-TZP) by three-dimensional profilometric assessment. Blocks of pre-sintered Y-TZP were cut providing 63 standard 5-mm-thick samples which were divided by surface treatment, as follows (n = 9): G50 (100 mJ/10 Hz/1 W-50 mu s); G100 (-100 mu s); G300 (-300 mu s); G600 (-600 mu s); G1000 (-1000 mu s); GTC (tribochemical silica coating); and GNC (untreated). After treated or not, samples were sintered according to the manufacturer's recommendations. Roughness, volume loss and step height were analyzed by 3D profilometric assessment with confocal laser microscopy. ANOVA and Tukey's test (p < 0.05) detected that irradiated groups showed increased roughness in the groups G50, G100, G300, and G600 when compared to GTC and GNC groups. The G1000 group showed a completely flat and unfavorable surface for retention. The groups G50, G100, and G300 showed great loss of volume and the step height formed, which can lead to a gap on the crowns. In G600 was observed satisfactory roughness with little loss of volume and the step height formed similar to GTC. Irrespective of laser protocol, any of the specimens showed the presence of cracks. It is suggested that the pulse width 600 mu s (G600) is the most suitable pulse width protocol as an alternative surface treatment, promoting micro-retention, with little loss of volume of material, comparable to silica coating treatment. (AU)

Processo FAPESP: 12/15141-6 - Investigação de parâmetros do laser de Er:YAG (SSP) para aumentar adesão à dentina afetada por cárie: estudo longitudinal
Beneficiário:Adriana Bona Matos
Linha de fomento: Auxílio à Pesquisa - Regular
Processo FAPESP: 15/13571-1 - Ação da largura de pulso do Laser de Er:YAG em dentina e materiais restauradores estéticos
Beneficiário:Adriana Bona Matos
Linha de fomento: Auxílio à Pesquisa - Regular