Highly nonlinear Pb2P2O7-Nb2O5 glasses for optical fiber production

Texto completo
Autor(es):
Manzani, Danilo [1] ; Gualberto, Tiago [2] ; Almeida, Juliana M. P. [2] ; Montesso, Murilo [3] ; Mendonca, Cleber R. [2] ; Rivera, Victor A. G. [2] ; De Boni, Leonardo [2] ; Nalin, Marcelo [1] ; Ribeiro, Sidney J. L. [1]
Número total de Autores: 9
Afiliação do(s) autor(es):
[1] Univ Estadual Paulista UNESP, Inst Quim, CP 355, BR-14801970 Araraquara, SP - Brazil
[2] Univ Sao Paulo, Sao Carlos Inst Phys, Sao Carlos, SP - Brazil
[3] Univ Fed Sao Carlos, Dept Chem, BR-13560 Sao Carlos, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: Journal of Non-Crystalline Solids; v. 443, p. 82-90, JUL 1 2016.
Citações Web of Science: 9
Resumo

In this study we present the production and characterization of Pb2P2O7-Nb2O5 glasses and optical fibers. The dependence of Nb2O5 content on thermal, structural and optical properties were investigated by thermal analysis (DSC), Raman spectroscopy, IN-Visible absorption, M-Lines and Z-scan techniques. Glass transition temperature (T-g) increased linearly with Nb2O5 content up to 60 mol%, while thermal stability against crystallization (AT) reached a maximum value of 225 C at 40 mol% of Nb2O5. Raman spectra showed a significant structural change by the insertion of Nb06 octahedral units in the glass network. The increase of Nb2O5 concentration shifts the glasses absorption edge to lower energies, and also increases the linear refractive indexes (no) due to the high polarizability of niobium atoms and formation of non -bridging oxygen. Similarly to no, an increase in the positive values of nonlinear refractive indexes was observed using Z-Scan technique with increase of Nb205 content, based on structural changes caused by the replacement of Pb2P2O7 instead Nb205. The average of n(2) values at 500-1500 nm raised from 2.2 x 10(-19) to 3.8 x 10(-19) m(2)/W, when the Nb2O5 content was increased from 10 to 60 mol%. Lastly, a core -cladding preform was produced by suction method and the optical fiber drawn. The sample containing 40 mol% of Nb2O5 was used for presenting the highest thermal stability against crystallization and no values >2 from green to near-infrared wavelengths. Multimode step index fiber with good core circularity and concentricity was produced and the optical losses were determined by cut-back method at visible and near infrared ranges. (C) 2016 Elsevier B.V. All rights reserved. (AU)

Processo FAPESP: 10/20776-5 - Fibras ópticas especiais à base de óxido de telúrio para aplicações ópticas não lineares
Beneficiário:Danilo Manzani
Linha de fomento: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 13/07793-6 - CEPIV - Centro de Ensino, Pesquisa e Inovação em Vidros
Beneficiário:Edgar Dutra Zanotto
Linha de fomento: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs
Processo FAPESP: 11/12399-0 - Aplicações de pulsos de femtossegundos em óptica não linear: espectroscopia, formatação de pulsos e microfabricação
Beneficiário:Cleber Renato Mendonça
Linha de fomento: Auxílio à Pesquisa - Temático
Processo FAPESP: 11/21434-3 - Nanopartículas em vidros óxidos e calcogenetos: não linearidades ópticas e fabricação de guia de onda com pulsos de femtossegundos
Beneficiário:Juliana Mara Pinto de Almeida
Linha de fomento: Bolsas no Brasil - Doutorado