Dissociation Equilibrium and Charge Carrier Formation in Agl-AgPO3 Glasses

Texto completo
Autor(es):
Bragatto, Caio Barca ; Martins Rodrigues, Ana Candida
Número total de Autores: 2
Tipo de documento: Artigo Científico
Fonte: Journal of Physical Chemistry C; v. 121, n. 25, p. 13507-13514, JUN 29 2017.
Citações Web of Science: 2
Resumo

The xAgI-(1 - x)AgPO3 glass system exhibits a wide and well-known range of variation in silver ion conductivity with the AgI molar ratio, x, while the total concentration of Ag+ ions does not change significantly. We propose an interpretation to explain this effect, based on the fact that only a fraction of Ag+ cations are effective charge carriers and that their concentration is determined by a dissociation equilibrium of AgI in the AgPO3 glass. In this case, the ionic conductivity stems from the thermodynamic activity of silver iodide, a(AgI), dissolved in the AgPO3 glass. To verify this relationship experimentally, a(AgI) is determined from electromotive force measurements of solid-state cells in the temperature range of 2590 C. Our results reveal a linear dependence of silver ion conductivity on a(AgI) over 3 orders of magnitude. The substantial variations in a(AgI) observed with the increase in the AgI molar ratio x are justified assuming a regular solution model for the AgIAgPO3 mixture. (AU)

Processo FAPESP: 13/07793-6 - CEPIV - Centro de Ensino, Pesquisa e Inovação em Vidros
Beneficiário:Edgar Dutra Zanotto
Linha de fomento: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs
Processo FAPESP: 11/10564-3 - Aspectos termodinâmicos da condutividade iônica em vidros
Beneficiário:Ana Candida Martins Rodrigues
Linha de fomento: Auxílio à Pesquisa - Regular