Ethanol electrooxidation using Ti/(RuO2)(x) Pt(1-x) electrodes prepared by the polymeric precursor method

Autor(es)

R. G Freitas ^[1] ; L. F. Q. P Marchesi ^[2] ; M. R Forim ^[3] ; L. O. S Bulhões ; E. C Pereira ; M. C Santos ; R. T. S Oliveira

Afiliação do(s) autor(es)

^[1] Universidade Federal de São Carlos. Departamento de Química

^[2] Universidade Federal de São Carlos. Departamento de Química

^[3] Universidade Federal de São Carlos. Departamento de Química

• Tipo de documento: Artigo Científico
• Fonte: Journal of the Brazilian Chemical Society; v. 22, n. 9, p. 1709-1717, 2011-09-00.

Resumo

This work describes a detailed study of the ethanol electrooxidation on Ti/(RuO2)(x)Pt(1-x) electrodes using several compositions prepared by the polymeric precursor method. The results obtained using cyclic voltammetry and chronoamperometry showed that the best composition of Ti/(RuO2)(x)Pt(1-x) electrodes for CO and ethanol oxidation processes is Ti/(RuO2)0.50Pt0.50. On this electrode composition the onset of CO and the ethanol oxidation occurred at 380 mV and 220 mV more negative than on Ti/Pt, respectively. Besides, there was an increase of 2.5-fold in the current density for ethanol electrooxidation under constant potential polarization. The Ti/(RuO2)0.50Pt0.50 electrodes produced lower amount of acetic acid compared to Ti/Pt and polycrystalline Pt electrodes using in situ HPLC spectrometric analysis. Also, a non common product from ethanol oxidation could be observed on higher RuO2 loads: ethyl acetate. Finally, the impedance data showed that Ti/(RuO2)0.50Pt0.50 electrode composition had the smallest charge transfer resistance for ethanol oxidation among those compositions investigated (AU)

• Processo FAPESP: 03/09933-8 - Núcleo de Excelência em Materiais Nanoestruturados Fabricados Eletroquimicamente
• Beneficiário: Ernesto Chaves Pereira de Souza
• Modalidade de apoio: Auxílio à Pesquisa - Programa PRONEX - Temático
• Processo FAPESP: 05/59992-6 - Materiais nanoestruturados: eletrocatálise e membranas de óxidos
• Beneficiário: Mauro Coelho dos Santos
• Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
• Processo FAPESP: 10/05555-2 - Investigação da formação eletroquímica de nanotubos-TiO2 e sua aplicação em sistemas conversores de energia nanoarquiteturados
• Beneficiário: Renato Garcia de Freitas Sobrinho
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado