Effect of the Cooling Rate on the Properties of Veneer Porcelain for Zirconia Dental Prosthesis

Autor(es)

Antonio Alves de Almeida Junior ^[1] ; Diogo Longhini ^[2] ; Paulo Atsushi Suzuki ^[3] ; Sebastião Ribeiro ^[4] ; Claudinei Santos ^[5] ; Gelson Luis Adabo ^[6]

Afiliação do(s) autor(es)

^[1] Universidade Estadual Paulista - UNESP. Faculdade de Odontologia de Araraquara. Departamento de Materiais Odontológicos e Prótese - Brasil

^[2] Universidade Estadual Paulista - UNESP. Faculdade de Odontologia de Araraquara. Departamento de Materiais Odontológicos e Prótese - Brasil

^[3] Universidade de São Paulo - USP. Escola de Engenharia de Lorena. Departamento de Engenharia de Materiais - Brasil

^[4] Universidade de São Paulo - USP. Escola de Engenharia de Lorena. Departamento de Engenharia de Materiais - Brasil

^[5] Universidade Estadual do Rio de Janeiro - UERJ. Faculdade de Tecnologia de Resende. Departamento de Engenharia de Materiais - Brasil

^[6] Universidade Estadual Paulista - UNESP. Faculdade de Odontologia de Araraquara. Departamento de Materiais Odontológicos e Prótese - Brasil

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 20, n. 5, p. 1418-1424, 2017-08-07.

Resumo

To solve chipping of veneer porcelain in zirconia dental prosthesis it has been studied different cooling rates in firing schedules to control residual stresses generated by differences in thermal properties between the ceramics. However, cooling rates may affect the porcelain, irrespectively of interaction with zirconia. This study analyzed the effect of cooling rate on the three-point flexural strength (FS), residual stress, Vickers hardness (VH) and V-notch fracture toughness (SEVNB) on a feldspathic porcelain (Vita VM9) indicated for covering zirconia. Bar-shaped specimens were sintered according manufacturer's schedule firing and cooled at different rates (slow, normal or fast). Specimens were tested for FS (n=30), VH (n=15) and SEVNB tests (n=15). Weibull analysis were performed from FS values to measure reliability and probability of failure (PF). One-way ANOVA was significant for VH (p<0.001), and Tukey's test showed that slow cooling led to higher values. There was no significant difference for FS (p=0.654) and SEVNB (p=0.734). Fast cooling led to the lowest PF, but cooling rate factor was not significant for Weibull modulus. All cooling group showed residual tensile stress (MPa): Slow = 34.81; Normal = 27.04; Fast = 18,98. It was concluded that cooling rate produce minor changes in the porcelain properties. (AU)

• Processo FAPESP: 09/17735-8 - Efeito de diferentes taxas de resfriamento sobre a cerâmica feldspática de cobertura para infraestruturas em zircônia
• Beneficiário: Antonio Alves de Almeida Junior
• Modalidade de apoio: Bolsas no Brasil - Doutorado
• Processo FAPESP: 10/05469-9 - Efeito de diferentes taxas de resfriamento sobre a cerâmica feldspática de cobertura para infra-estruturas em zircônia
• Beneficiário: Gelson Luis Adabo
• Modalidade de apoio: Auxílio à Pesquisa - Regular