Dentin bond strength and nanoleakage of the adhesive interface after intracoronal bleaching

Texto completo
Autor(es):
Cavalli, Vanessa [1] ; Sebold, Maicon [1] ; Shinohara, Mirela Sanae [2] ; Pereira, Patricia Nobrega Rodrigues [3] ; Giannini, Marcelo [1]
Número total de Autores: 5
Afiliação do(s) autor(es):
[1] Univ Estadual Campinas, Piracicaba Dent Sch, Operat Dent Div, Dept Restorat Dent, Ave Limeira 901, BR-13414018 Piracicaba, SP - Brazil
[2] Univ Estadual Campinas, Piracicaba Dent Sch, Dent Mat Div, Dept Restorat Dent, BR-13414018 Piracicaba, SP - Brazil
[3] Univ Florida, Coll Dent, Operat Dent Div, Dept Restorat Dent Sci, Gainesville, FL 32610 - USA
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: MICROSCOPY RESEARCH AND TECHNIQUE; v. 81, n. 4, p. 428-436, APR 2018.
Citações Web of Science: 0
Resumo

This study evaluated dentin bond strength (BS) and nanoleakage of non- and pre-etched dentin immediately (T-0,), 7 days (T-7), and 14 days (T-14) after bleaching. Bovine incisors (150) were selected and half of them submitted to intrapulpal dentin etching (e). Non- and pre-etched dentin were subjected to the following (n=15): no bleaching/control (C); 35% carbamide peroxide (CP); 35% hydrogen peroxide (35% HP); 25% hydrogen peroxide (25% HP); and sodium perborate (SP). Bleaching agents were applied to the pulp chamber four times within a 72-h interval. Afterwards, pulp chamber dentin was prepared for the BS test at different evaluation times (n=5): T-0, T-7, and T-14. Composite blocks were built on pulp chamber and sectioned in slices. Slices were reduced to an hour-glass shape with a cross-sectional area of 0.8 mm(2) and submitted to microtensile BS test. Two additional specimens for each group were prepared for nanoleakage evaluation by transmission electron microscopy (TEM). Results were analyzed by ANOVA (two-way) and Dunnett's test (p<.05). BS decreased immediately after intracoronal bleaching for both sound and pre-etched dentin (p<.05). At T-14, the BS of non-etched bleached dentin increased for all groups, whereas the pre-etched SPe group presented BS similar to the Ce. Nanoleakage within the hybrid layer was perceptible immediately after bleaching, although a decrease in nanoleakage was observed for all groups at T-14. Adhesive restorations should be performed 7-14 days after bleaching, according to the bleaching agent used. Intracoronal bleaching should be performed preferably with sodium perborate if previous dentin etching is applied. (AU)