Polymerization shrinkage evaluation in experimental dental composite filled with montmorillonite nanoparticles

Texto completo
Autor(es):
Campos, Luiza M. P. [1] ; Boaro, Leticia C. [2] ; Santos, Tamiris M. R. [1] ; Santos, Vinicius J. [1] ; Grecco-Romano, Rebeca [1] ; Santos, Mariana J. [1] ; Parra, Duclerc F. [1]
Número total de Autores: 7
Afiliação do(s) autor(es):
[1] CNEN SP, IPEN, Nucl & Energy Res Inst, Av Prof Lineu Prestes 2242, BR-05508000 Sao Paulo, SP - Brazil
[2] Univ Santo Amaro, Sch Dent, R Prof Eneas Siqueira Neto 340, BR-04829300 Sao Paulo, SP - Brazil
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY; v. 131, n. 1, p. 771-774, JAN 2018.
Citações Web of Science: 2
Resumo

This study aimed to develop experimental dental restorative composites by the addition of montmorillonite (MMT) nanoparticles in a polymeric matrix-based BisGMA/TEGDMA, to assess the possibility of a different dimensional behavior during the photo-polymerization. The characterization of experimental composites was established with the following analyses: thermal-mechanical analysis (TMA), X-ray diffraction (XRD) and transmission electron microscopy. Data for TMA were analyzed using one-way ANOVA and Tukey test (p < 0.05). It was observed that the experimental composites filled with MMT nanoparticle showed statistically similar polymerization shrinkage values (by TMA analysis) in the concentration of 30% and statistically lower polymerization shrinkage values in the concentration of 50%, compared to composites filled with barium glass (BG-control groups). These results may be related to the interaction polymeric matrix/MMT nanoparticles and the formation of nanocomposites, observed by XRD and TEM analyses. (AU)

Processo FAPESP: 16/19254-0 - Síntese e caracterização de hidrogéis de poli (N-vinil-2-pirrolidona) contendo argila laponite RD para modulação da liberação de neomicina/nano prata
Beneficiário:Vinicius Juvino dos Santos
Linha de fomento: Bolsas no Brasil - Mestrado
Processo FAPESP: 13/07229-3 - Estudo da adição de nanopartículas argilominerais em matrizes poliméricas fotoativadas a base de bisgma/tegdma, aplicadas à odontologia.
Beneficiário:Luiza Mello de Paiva Campos
Linha de fomento: Bolsas no Brasil - Pós-Doutorado