Phase transformation of Nb2O5 during the formation of flame sprayed coatings and its influence on the adhesion strength, abrasive wear and slurry erosive wear

Texto completo
Autor(es):
Carvajal Fals, Hipolito [1] ; Xavier Belem, Maria Julia [2] ; Sanchez Roca, Angel [1] ; Fanton, Leonardo [3] ; Camello Lima, Carlos Roberto [2]
Número total de Autores: 5
Afiliação do(s) autor(es):
[1] Oriente Univ, Coll Mech & Ind Engn, Santiago De Cuba - Cuba
[2] Univ Metodista Piracicaba, Prod Engn Grad Program, Rod Luis Ometto, Km 24, BR-13451900 Santa Barbara Doeste, SP - Brazil
[3] Univ Estadual Campinas, Rua Mendeleyev 200, BR-13083860 Campinas, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: WEAR; v. 426, n. A, p. 277-284, APR 30 2019.
Citações Web of Science: 1
Resumo

The development of research related to the characterization of niobium pentoxide (Nb2O5) has been of great interest in the scientific and commercial community due to promising performances in bio-electrochemical applications, advanced catalysts and corrosive environments. In this work, layers of 250 mu m, 350 mu m and 550 mu m of Nb2O5 were deposited by low-speed flame spray on NiAl-bond coated AISI 1020 steel substrates. The phase transformations of Nb2O5, which occur during the formation of the layers, were studied as a function of deposited thickness and further correlated with adhesion, abrasion and slurry erosion resistance. X-ray diffraction analyzes of the coatings were performed for the study of the phases in the process. Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) with dispersive energy microanalysis (EDS) were used to help microstructural analysis. The adhesive strength of the layers was evaluated by ASTM C633-13 and correlated with abrasion (ASTM G65-16) and slurry erosion wear resistance. From the microscopy analysis, a dense layer was observed with good interconnection at the interface Nb2O5 -NiAl, with presence of pores typical of the thermal spray process. The XRD diffractograms of the niobium oxide coated samples show similar results regardless of the coating thickness (250, 350 and 550 mu m) presenting superior compatibility with the hexagonal Nb2O5 and the monoclinic NbO2.46 (Nb22O54). The significantly higher intensities of the hexagonal Nb2O5 peaks suggest that it is the predominant phase. The thinner coatings, 250 and 350 mu m, had higher adhesive strength, with a mean fracture stress of 16.12 MPa and 15.27 MPa, respectively. Nb2O5 thinner coatings showed also higher abrasive wear resistance when compared to ``D2{''} tool steel and ``H13{''} chrome tool steel. The thicker coatings (550 mu m) had a mean adhesive strength of 13.73 MPa. From the abrasive wear tests, thicker coatings showed a greater volume loss of 41.18 mm(3). The 550 mu m coating presented higher slurry erosion resistance at a 30 degrees particle impact angle, with a lower volume loss (12.93 mm(3)). (AU)

Processo FAPESP: 17/16715-0 - Evolução da textura cristalográfica gerada por laminação e recristalização da liga Ti-35Nb-7Zr-5Ta e seu efeito no crescimento de nanotubos de TiO2
Beneficiário:Leonardo Fanton
Linha de fomento: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 17/25363-0 - Influência da adesão de revestimentos aplicados por distintos processos de aspersão térmica sobre suas propriedades de desgaste e corrosão
Beneficiário:Carlos Roberto Camello Lima
Linha de fomento: Auxílio à Pesquisa - Pesquisador Visitante - Internacional