In Situ 2D Perovskite Formation and the Impact of the 2D/3D Structures on Performance and Stability of Perovskite Solar Cells

Texto completo
Autor(es):
de Holanda, Matheus S. [1] ; Szostak, Rodrigo [1] ; Marchezi, Paulo E. [1] ; Duarte, Luis G. T. A. [1] ; Germino, Jose C. [1] ; Atvars, Teresa D. Z. [1] ; Nogueira, Ana F. [1]
Número total de Autores: 7
Afiliação do(s) autor(es):
[1] Univ Campinas UNICAMP, Chem Inst, Lab Nanotecnol & Energia Solar, POB 6154, BR-13083970 Campinas, SP - Brazil
Número total de Afiliações: 1
Tipo de documento: Artigo Científico
Fonte: SOLAR RRL; v. 3, n. 9, SI JULY 2019.
Citações Web of Science: 2
Resumo

Hybrid organic and inorganic perovskite solar cells lack long-term stability, and this negatively impacts the widespread application of this emerging and promising photovoltaic technology. Herein, aiming to increase the stability of perovskite films based on CH3NH3PbI3 and to deeply understand the formation of 2D structures, solutions of alkylammonium chlorides containing 8, 10, and 12 carbons are introduced during the spin-coating on the surface of 3D perovskite films leading to the in situ formation of 2D structures. It is possible to identify the chemical formulae of some 2D structures formed by X-ray diffraction and UV-vis analysis of the modified films. Interestingly, the increase in the stability of the CH3NH3PbI3 films due to the formation of a 2D + 3D perovskite network is only possible in planar TiO2 substrates. The increase in stability of the CH3NH3PbI3 films follows the surfactant molecule order: octylammonium (8C) > decylammonium (1 degrees C) > dodecylammonium (12C) chlorides > standard. An increase of 17.6% in the lifetime of the devices assembled with octylammonium-modified perovskite film is observed compared with that of the standard device, which is directly linked to the improvement of the charge carrier lifetimes obtained from time-correlated single photon counting measurements. (AU)

Processo FAPESP: 17/11986-5 - Divisão de Pesquisa 1 - portadores densos de energia
Beneficiário:Ana Flávia Nogueira
Linha de fomento: Auxílio à Pesquisa - Programa Centros de Pesquisa em Engenharia
Processo FAPESP: 17/12582-5 - Perovskitas com cátions mistos: relação entre estrutura, composição, propriedades eletrônicas e eficiência das células solares
Beneficiário:Rodrigo Szostak
Linha de fomento: Bolsas no Brasil - Doutorado
Processo FAPESP: 13/16245-2 - Propriedades fotofísicas de filmes finos de polímeros conjugados
Beneficiário:Teresa Dib Zambon Atvars
Linha de fomento: Auxílio à Pesquisa - Regular