Synthesis of functionalized mesoporous material from rice husk ash and its application in the removal of the polycyclic aromatic hydrocarbons

Autor(es)

Costa, Jose Arnaldo S. ^{[1, 2]} ; Sarmento, Victor H. V. ^[3] ; Romao, Luciane P. C. ^[4] ; Paranhos, Caio M. ^[2]

Afiliação do(s) autor(es)

^[1] Univ Aveiro, Dept Chem, CICECO, P-3810193 Aveiro - Portugal

^[2] Univ Fed Sao Carlos, Polymer Lab, Dept Chem, BR-13565905 Sao Carlos, SP - Brazil

^[3] Univ Fed Sergipe, Dept Chem, BR-49100000 Itabaiana, Sergipe - Brazil

^[4] Univ Fed Sergipe, Dept Chem, BR-49100000 Sao Cristovao, Sergipe - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Environmental Science and Pollution Research; v. 26, n. 25, p. 25476-25490, SEP 2019.
• Citações Web of Science: 2

Resumo

The rice husk ash (RHA) was used as an alternative source of silica for the synthesis of the functionalized mesoporous material, which was used in the removal of the PAHs naphthalene (Nap), benzo{[}b]fluoranthene (B{[}b]F), benzo{[}k]fluoranthene (B{[}k]F), and benzo{[}a]pyrene (B{[}a]P) from aqueous media. The PABA-MCM-41 (RHA) was characterized using FTIR, TGA, SAXS, and N-2 adsorption-desorption analyses. Removal experiments were performed to determine the initial concentrations, individual adsorption in comparison with the mixture of the PAHs, PABA-MCM-41 (RHA) amount, pH, time, and temperature, and the results obtained were statistically analyzed. The PABA-MCM-41 (RHA) presented the S-BET, V-T, and D-BJH values of 438 m(2) g(-1), 0.41 cm(3) g(-1), and 3.59 nm, respectively, and good thermal stability. The q(e) values found in the kinetic equilibrium for the PAHs mixture followed increasing order: Nap < B{[}a] P < B{[}k]F < B{[}b]F, with removal percentages of 89.08 +/- 0.00, 93.85 +/- 0.28, 94.54 +/- 0.10, and 97.80 +/- 0.05%, respectively. (AU)

• Processo FAPESP: 18/18894-1 - Síntese de materiais mesoporosos bioativos para utilização em biomedicina regenerativa
• Beneficiário: José Arnaldo Santana Costa
• Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Pós-Doutorado
• Processo FAPESP: 14/05679-4 - Desenvolvimento de materiais mesoporosos baseados em sílica oriunda de biomassa para utilização como sistema remediador de hidrocarbonetos policíclicos aromáticos (HPAs)
• Beneficiário: José Arnaldo Santana Costa
• Modalidade de apoio: Bolsas no Brasil - Doutorado
• Processo FAPESP: 17/06775-5 - Desenvolvimento de membranas poliméricas híbridas tunáveis na remediação de hidrocarbonetos policíclicos aromáticos (HPAs) oriundos do petróleo
• Beneficiário: José Arnaldo Santana Costa
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais
• Beneficiário: Elson Longo da Silva
• Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs