Ultrafine eutectic coatings from Fe-Nb-B powder using laser cladding

Texto completo
Autor(es):
Caneda, Chaiane M. [1, 2] ; Fogagnolo, Joao B. [3] ; Kiminami, Claudio S. [1] ; Afonso, Conrado R. M. [1]
Número total de Autores: 4
Afiliação do(s) autor(es):
[1] Univ Fed Sao Carlos UFSCar, Dept Engn Mat DEMa, Rod Washington Luis, Km 235, BR-13565905 Sao Carlos, SP - Brazil
[2] Univ Fed Sao Carlos UFSCar, Grad Program Mat Sci & Engn PPG CEM, Rod Washington Luis, Km 235, BR-13565905 Sao Carlos, SP - Brazil
[3] Univ Estadual Campinas, UNICAMP, FEM, Rua Mendeleyev 200, BR-13083860 Campinas, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: MATERIALS CHARACTERIZATION; v. 160, FEB 2020.
Citações Web of Science: 0
Resumo

In this paper, a laser cladding process was proposed to obtain ultrafine eutectic Fe-Nb-B alloy coatings on AISI 1020 steel substrate in which the power and scanning speed were defined. The laser cladding process can be used as a rapid solidification processing route to produce single laser tracks and coatings (overlapped tracks) with preplaced powders deposited onto a mild steel substrate in order to obtain a minimal dilution between the coating/substrate. This research aims to produce a coating of Fe74.25Nb8.25B17.5 (at.%) alloy over the AISI 1020 steel substrate by laser cladding using a pre-placed powder method to investigate the parameters on coating production, dilution, microstructure, and properties. The final goal is to find an appropriate processing parameter range to obtain coatings with high hardness and possibly good wear resistance. The microstructure and behavior of powder, cladding layers and coatings were examined by X-ray Diffractometry, Differential Scanning Calorimetry, Scanning Electron Microscopy and Transmission Electron Microscopy of selected samples prepared with a Dual Beam microscope using a Focused Ion Beam. For the processing conditions used, the coatings showed larger exothermic crystallization peaks. The results of microhardness from coatings showed values of hardness over 700 HV. (AU)

Processo FAPESP: 15/19978-6 - Caracterização avançada através de TEM de amostras preparadas por FIB de recobrimentos de ligas nanocristalinas produzidos por aspersão térmica e laser cladding
Beneficiário:Conrado Ramos Moreira Afonso
Linha de fomento: Bolsas no Exterior - Pesquisa
Processo FAPESP: 13/05987-8 - Processamento e caracterização de ligas metálicas amorfas, metaestáveis e nano-estruturadas
Beneficiário:Claudio Shyinti Kiminami
Linha de fomento: Auxílio à Pesquisa - Temático