Experimental Investigation of Delta Phase Precipitation in Inconel 625 Superalloy Aged at 550, 625 and 725 °C

Texto completo
Autor(es):
Renato Baldan ; Antonio Augusto Araujo Pinto da Silva ; Tiemi Manfio Tanno ; Eliara Torres da Costa ; João Victor Negri Brentegani ; Antonio Augusto Couto
Número total de Autores: 6
Tipo de documento: Artigo Científico
Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 23, n. 1, p. -, 2020.
Resumo

Abstract The δ is an important stable phase that replaces the metastable γ'' in the microstructure of Inconel 625 superalloy. The present work aims to investigate the kinetic of δ-phase precipitation in the microstructure of Inconel 625 nickel-based superalloy aged at 550, 625 and 725 °C up to 1000 h. Aging temperatures were chosen based on the thermodynamic simulation using JMatPro software which indicated that this phase is stable at temperatures below 905 °C. Microstructure of the heat-treated samples was analyzed via SEM/EDS and microhardness evolution was performed by Vickers microhardness tests. The results have shown that the samples aged at 550 °C (all times), 625 °C (all times) and 725 °C up to 200 h did not presented microstructural evidences of δ precipitation. However, samples aged at 725 °C for 500 and 1000 h clearly presented an acicular δ-phase precipitated mainly at the grain boundaries. It was noted changes in the microhardness at different aging time and temperatures probably due to the presence of γ'' and/or δ phases. The sample aged at 625 °C for 1000 h presented the highest microhardness value (333 ± 10 HV). (AU)

Processo FAPESP: 18/07802-9 - Caracterização microestrutural e estudo da resistência à oxidação isotérmica e cíclica em elevadas temperaturas das superligas MAR-M246 convencional e modificada com nióbio