Alumina-toughened zirconia for dental applications: Physicochemical, mechanical, optical, and residual stress characterization after artificial aging

Texto completo
Autor(es):
Bergamo, Edmara T. P. [1] ; Cardoso, Karina B. [1] ; Lino, Lucas F. O. [1] ; Campos, Tiago M. B. [2] ; Monteiro, Kelli N. [3] ; Cesar, Paulo F. [3] ; Genova, Luis A. [4] ; Thim, Gilmar P. [2] ; Coelho, Paulo G. [5] ; Bonfante, Estevam A. [1]
Número total de Autores: 10
Afiliação do(s) autor(es):
[1] Univ Sao Paulo, Dept Prosthodont & Periodontol, Bauru Sch Dent, Al Otavio Pinheiro Brisola 9-75, BR-17012901 Bauru, SP - Brazil
[2] Aeronaut Technol Inst, Dept Phys, Sao Jose Dos Campos, SP - Brazil
[3] Univ Sao Paulo, Sch Dent, Dept Biomat & Oral Biol, Sao Paulo, SP - Brazil
[4] Inst Res Nucl Energy, Ctr Mat Sci & Technol, Sao Paulo, SP - Brazil
[5] NYU, Dept Biomat & Biomimet, Hansjorg Wyss Dept Plast Surg Mech & Aerosp Engn, New York, NY - USA
Número total de Afiliações: 5
Tipo de documento: Artigo Científico
Fonte: JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS; DEC 2020.
Citações Web of Science: 0
Resumo

To characterize the physicomechanical properties of an alumina-toughened zirconia (ATZ). ATZ synthesis consisted of the addition of alumina particles in an yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP) matrix. Specimens were obtained by uniaxial and isostatic pressing ATZ and 3Y-TZP powders and sintering at 1600 degrees C/1 h and 1550 degrees C/1 h, respectively. Crystalline content and residual stress were evaluated using X-ray diffraction (XRD). Microstructure was characterized by scanning electron microscopy (SEM). Optical properties were determined by reflectance test. Mechanical properties were assessed by biaxial flexural strength test. All analyses were performed before and after aging (134 degrees C, 20 h, 2 bar). XRD and SEM revealed a typical ATZ and 3Y-TZP crystalline content, chiefly tetragonal phase, with a dense polycrystalline matrix, though a smaller grain size for ATZ. Aging triggered a similar monoclinic transformation for both systems; however, ATZ exhibited higher residual compressive stresses than 3Y-TZP. While as-processed 3Y-TZP demonstrated significantly higher characteristic strength relative to ATZ, no significant difference was observed after aging (similar to 215 MPa increase in the ATZ strength). ATZ presented significantly higher opacity relative to 3Y-TZP, although aging significantly increased the translucency of both systems (increase difference significantly higher in the 3Y-TZP compared to ATZ). ATZ physicomechanical properties support its applicability in the dental field, with a lower detrimental effect of aging relative to 3Y-TZP. (AU)

Processo FAPESP: 18/19094-9 - Compósitos experimentais 80%ZrO2 -20%Al2O3: caracterização microestrutural, óptica e de sobrevida
Beneficiário:Lucas Fracassi de Oliveira Lino
Linha de fomento: Bolsas no Brasil - Mestrado
Processo FAPESP: 16/18818-8 - EMU concedido no processo 2012/19078-7: ElectroPuls E3000 Linear-Torsion All-Electric dynamic test instrument package
Beneficiário:Estevam Augusto Bonfante
Linha de fomento: Auxílio à Pesquisa - Programa Equipamentos Multiusuários
Processo FAPESP: 12/19078-7 - Desenvolvimento e processamento de compósito de Al2O3-ZrO2 para próteses monolíticas CAD/CAM: efeito do envelhecimento na resistência à flexão biaxial
Beneficiário:Estevam Augusto Bonfante
Linha de fomento: Auxílio à Pesquisa - Apoio a Jovens Pesquisadores
Processo FAPESP: 19/08693-1 - Compósitos experimentais à base de alumina e zircônia infiltrados por vidro: caracterização microestrutural e das propriedades ópticas e mecânicas.
Beneficiário:Edmara Tatiely Pedroso Bergamo
Linha de fomento: Bolsas no Brasil - Pós-Doutorado