Influence of Abutment Fabrication Method on 3D Fit at the Implant-Abutment Connection

Texto completo
Autor(es):
Ramalho, Ilana [1] ; Witek, Lukasz [2] ; Coelho, Paulo G. [2] ; Bergamo, Edmara [1] ; Pegoraro, Luiz Fernando [1] ; Bonfante, Estevam A. [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Univ Sao Paulo Bauru, Dept Prosthodont & Periodontol, Sch Dent, Bauru, SP - Brazil
[2] NYU, Dept Biomat & Biomimet, New York, NY - USA
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: International Journal of Prosthodontics; v. 33, n. 6, p. 641-647, NOV-DEC 2020.
Citações Web of Science: 0
Resumo

Purpose: To three-dimensionally evaluate the internal fit at the implant-abutment interface of abutments fabricated with different workflows using a combination of the silicone replica technique and microcomputed tomography (mu CT). Materials and Methods: Thirty abutments were fabricated to restore internal-connection implants and were divided into three groups according to fabrication method: (1) full digital (abutment machined using CAD/CAM system); (2) Ti-Base (prefabricated standard Ti-Base abutments); and (3) UCLA (UCLA-type abutments) (n = 10/group). Linear and volume measurements were performed to assess the internal misfit using a silicone replica of the implant-abutment interface misfit area, which was three-dimensionally reconstructed after mu CT. The internal discrepancies in three different regions of interest (Gap(superior), Gap(marginal), and Gap(center)) were assessed. Data were statistically evaluated using ANOVA and Tukey test (P < .05). Results: Ti-Base and UCLA abutments presented significantly lower misfit volume (0.49 mm(3), 95% CI: +/- 0.045 mm(3) and 0.48 mm(3), 95% CI: +/- 0.045 mm(3), respectively) and mean internal gap (25.20 mu m, 95% CI: +/- 3.14 mu m and 27.97 mu m, 95% CI: +/- 3.14 mu m, respectively) than the full digital group (0.70 mm(3), 95% CI: +/- 0.045 mm(3); 34.90 mu m, 95% CI: +/- 3.14 mu m) (P < .001), but did not differ from each other (P = .825). While Gap(center) was significantly higher in the full digital group (P < .001), Gap(superior) and Gap(marginal) did not demonstrate significant differences among groups. All regions were statistically similar within groups, except for Gap(center) in the full digital group, which exhibited higher mean values compared to the other regions (P = .000). The 3D measurements for quantification of internal discrepancy were strongly associated with the 2D measurements. Conclusion: Ti-Base and UCLA abutments exhibited better internal fit at the implant-abutment interfaces compared to a fully digitalized workflow (CAD/CAM custom abutments). (AU)

Processo FAPESP: 17/19362-0 - DESENVOLVIMENTO E CARACTERIZAÇÃO MECÂNICA E ÓPTICA DE COMPÓSITO 80% Al2O3 e 20% ZrO2 TRANSLÚCIDA PARA PRÓTESES MONOLÍTICAS CAD/CAM
Beneficiário:Adolfo Coelho de Oliveira Lopes
Linha de fomento: Bolsas no Exterior - Estágio de Pesquisa - Mestrado
Processo FAPESP: 19/08693-1 - Compósitos experimentais à base de alumina e zircônia infiltrados por vidro: caracterização microestrutural e das propriedades ópticas e mecânicas.
Beneficiário:Edmara Tatiely Pedroso Bergamo
Linha de fomento: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 16/18818-8 - EMU concedido no processo 2012/19078-7: ElectroPuls E3000 Linear-Torsion All-Electric dynamic test instrument package
Beneficiário:Estevam Augusto Bonfante
Linha de fomento: Auxílio à Pesquisa - Programa Equipamentos Multiusuários
Processo FAPESP: 12/19078-7 - Desenvolvimento e processamento de compósito de Al2O3-ZrO2 para próteses monolíticas CAD/CAM: efeito do envelhecimento na resistência à flexão biaxial
Beneficiário:Estevam Augusto Bonfante
Linha de fomento: Auxílio à Pesquisa - Jovens Pesquisadores
Processo FAPESP: 19/14798-0 - Desenvolvimento de blocos pré sinterizados de compósito ZTA - 80%Al2O3/20%ZrO2 para fresagem em sistema CAD/CAM
Beneficiário:Adolfo Coelho de Oliveira Lopes
Linha de fomento: Bolsas no Brasil - Doutorado
Processo FAPESP: 16/17793-1 - Desenvolvimento e caracterização mecânica e óptica de compósito 80% Al2O3 e 20% ZrO2 translúcida para próteses monolíticas CAD/CAM
Beneficiário:Adolfo Coelho de Oliveira Lopes
Linha de fomento: Bolsas no Brasil - Mestrado