| Tipo de documento: | Artigo Científico |
| Fonte: | JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS; v. 133, p. 10-pg., 2022-07-12. |
| Resumo | |
Purpose: To evaluate the effect of composition, fabrication mode, and thermal cycling on the mechanical properties of different polymeric systems used for temporary dental prostheses. Materials and methods: Standard bar-shaped specimens (25 x 2 x 2 mm) were fabricated of six polymeric systems of varying compositions and fabrication modes (n = 10/group): conventional PMMA (Alike, GC) - group CGC; conventional PMMA (Dencor, Cl ' assico) - group CD; bis-acryl (Tempsmart, GC) - group BGC; bis-acryl (Yprov, Yller) - group BY; milled PMMA (TelioCAD, Ivoclar) - group MI; 3D printed bis-acryl - (Cosmos Temp, Yller) group PY. Half of the specimens were subjected to 5000 thermal cycles (5 degrees C to 55 degrees C). Three-point bending tests were performed using a universal testing machine with a crosshead speed set to 0.5 mm/min. Flexural strength and elastic modulus were calculated from the collected data. FTIR spectra were recorded pre and post curing and after thermal cycling to evaluate material composition and degree of conversion. Energy-dispersive spectroscopy (EDS) and scanning electron microscope (SEM) were utilized to examine the composition and micromorphology of the systems, respectively. Data were analyzed using two-analysis of variance and Tukey tests (alpha = 0.05). Results: FTIR spectra indicated that BGC, BY and PY groups corresponded to urethane dimethacrylate systems (bis-acryl), while CGC, CD, and MI groups corresponded to monomethacrylate systems, polymethyl methacrylate (PMMA). Bis-acryl BGC system yeilded the highest flexural strength (80 MPa), followed by the milled PMMA MI system (71 MPa), both statistically significant different relative to other groups. Bis-acryl BY exhibited the lowest flexural strength (27 MPa). Thermocycling significantly increased the flexural strength of all polymeric systems (-10-15 MPa), except for the 3D-printed PY group. Bis-acryl BGC (1.89 GPa) and conventional PMMA CGC (1.66 GPa) groups exhibited the highest elastic modulus, followed by milled PMMA MI group (1.51 GPa) and conventional PMMA CD (1.45 GPa) systems, with significant difference detected between BGC group and MI and CD groups. The 3D printed PY (0.78 GPa) and bis-acryl BY (0.47 GPa) systems presented the lowest elastic modulus. Thermocycling did not have a significant influence on the elastic modulus. FTIR spectra indicate water sorption and release of unreacted monomers as well as increased degree of conversion (-5-12%) after thermal cycling. Conclusion: Composition and fabrication mode and thermal cycling significantly affected the mechanical properties of polymeric systems used for temporary dental prostheses. (AU) | |
| Processo FAPESP: | 20/12874-9 - Infiltração gradada por vidro em um compósito experimental à base de whiskers de alumina e zircônia: desenvolvimento, caracterização microestrutural e das propriedades ópticas e mecânicas |
| Beneficiário: | Tiago Moreira Bastos Campos |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |
| Processo FAPESP: | 20/16500-6 - Síntese de um nanocompósito ATZ(80%ZrO2-20%Al2O3) e caracterização microestrutural, óptica e de sobrevida antes e após o envelhecimento |
| Beneficiário: | Mariana Miranda de Toledo Piza |
| Modalidade de apoio: | Bolsas no Brasil - Mestrado |
| Processo FAPESP: | 21/06730-7 - Rumo à zircônia sustentável reciclada a partir do descarte de usinagem e melhorada por infiltração graduada e ao desenvolvimento de blocos de zircônia multicamada resistentes, graduados, e não suscetíveis ao envelhecimento |
| Beneficiário: | Estevam Augusto Bonfante |
| Modalidade de apoio: | Auxílio à Pesquisa - Jovens Pesquisadores - Fase 2 |
| Processo FAPESP: | 19/08693-1 - Compósitos experimentais à base de alumina e zircônia infiltrados por vidro: caracterização microestrutural e das propriedades ópticas e mecânicas. |
| Beneficiário: | Edmara Tatiely Pedroso Bergamo |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |
| Processo FAPESP: | 22/07157-1 - Caracterização física e mecânica de um sistema multicamadas utilizando zircônia reciclada |
| Beneficiário: | Ernesto Byron Benalcazar Jalkh |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |
| Processo FAPESP: | 21/08018-2 - Caracterização nanomecânica de compósitos ZTA e ATZ infiltrados por vidro |
| Beneficiário: | Edmara Tatiely Pedroso Bergamo |
| Modalidade de apoio: | Bolsas no Exterior - Estágio de Pesquisa - Pós-Doutorado |
| Processo FAPESP: | 19/14798-0 - Desenvolvimento de blocos pré sinterizados de compósito ZTA - 80%Al2O3/20%ZrO2 para fresagem em sistema CAD/CAM |
| Beneficiário: | Adolfo Coelho de Oliveira Lopes |
| Modalidade de apoio: | Bolsas no Brasil - Doutorado |
| Processo FAPESP: | 16/18818-8 - EMU concedido no processo 2012/19078-7: ElectroPuls E3000 Linear-Torsion All-Electric dynamic test instrument package |
| Beneficiário: | Estevam Augusto Bonfante |
| Modalidade de apoio: | Auxílio à Pesquisa - Programa Equipamentos Multiusuários |