Structural Characterization of the Hot-rolled Ti-25Ta-xZr Alloys by Rietveld Method

Autor(es)

Pedro Akira Bazaglia Kuroda ^[1] ; Carlos Roberto Grandini ^[2] ; Conrado Ramos Moreira Afonso ^[3]

Afiliação do(s) autor(es)

^[1] Universidade Federal de São Carlos. Departamento de Engenharia de Materiais - Brasil

^[2] Universidade Estadual Paulista. Laboratório de Anelasticidade e Biomateriais - Brasil

^[3] Universidade Federal de São Carlos. Departamento de Engenharia de Materiais - Brasil

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 26, 2023-06-26.

Resumo

This paper aims to analyze the structure of the Ti-25Ta-xZr system alloys (x = 0, 10, 20, 30, and 40% wt.) after melting and hot-rolling by Rietveld's technique. The results confirm that zirconium acts as a β phase stabilizer (in which the Ti-25Ta-40Zr alloy is fully β in the as-cast condition), increases the lattice parameters of the phases, decreases the c/a ratio of the α phase, consequently, decreases the elastic modulus values (86 to 72GPa) and decreases the atomic packing factor (APF) of the alloys (60% reduction compared to alloys with and without zirconium in the as-cast condition and 50% reduction in the hot-rolled condition). Concerning hot-rolling, this mechanical process induces the α phase formation and increases the atomic packing factor of the alloys (APF). By the William-Hall technique, it was possible to calculate the average crystalline size and the micro-strain of the structures. (AU)

• Processo FAPESP: 18/18293-8 - Ligas de titânio: transformações de fases e manufatura aditiva aplicadas na obtenção de materiais com gradientes funcionais
• Beneficiário: Rubens Caram Junior
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 19/26517-6 - Influência da microestrutura e fases formadas na funcionalização da superfície de ligas beta Ti-25Ta-xZr
• Beneficiário: Pedro Akira Bazaglia Kuroda
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado