Physical Properties of an Acrylic Resin after Incorporation of an Antimicrobial Monomer

Texto completo
Autor(es):
Regis, Romulo Rocha [1] ; Zanini, Ana Paula ; Della Vecchia, Maria P. [1] ; Silva-Lovato, Claudia Helena [1] ; Oliveira Paranhos, Helena Freitas [1] ; de Souza, Raphael Freitas [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Univ Sao Paulo, Ribeirao Preto Dent Sch, Dept Dent Mat & Prosthodont, Ribeirao Preto - Brazil
Número total de Afiliações: 1
Tipo de documento: Artigo Científico
Fonte: JOURNAL OF PROSTHODONTICS-IMPLANT ESTHETIC AND RECONSTRUCTIVE DENTISTRY; v. 20, n. 5, p. 372-379, JUL 2011.
Citações Web of Science: 15
Resumo

Purpose: This study evaluated the effect of the incorporation of the antimicrobial monomer methacryloyloxyundecylpyridinium bromide (MUPB) on the hardness, roughness, flexural strength, and color stability of a denture base material. Materials and Methods: Ninety-six disk-shaped (14-mm diameter x 4-mm thick) and 30 rectangular (65 x 10 x 3.3 mm(3)) heat-polymerized acrylic resin specimens were divided into three groups according to the concentration of MUPB (w/w): (A) 0%, (B) 0.3%, (C) 0.6%. Hardness was assessed by a hardness tester equipped with a Vickers diamond penetrator. Flexural strength and surface roughness were tested on a universal testing machine and a surface roughness tester, respectively. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 36 days of immersion in water, coffee, or wine. Variables were analyzed by ANOVA/Tukey HSD test (alpha = 0.05). Results: The following mean results (+/-SD) were obtained for hardness (A: 15.6 +/- 0.6, B: 14.6 +/- 1.7, C: 14.8 +/- 0.8 VHN; ANOVA: p = 0.061), flexural strength (A: 111 +/- 17, B: 105 +/- 12, C: 88 +/- 12 MPa; ANOVA: p = 0.008), and roughness (A: 0.20 +/- 0.11, B: 0.20 +/- 0.11, C: 0.24 +/- 0.08 mu m; ANOVA: p = 0.829). Color changes of immersed specimens were significantly influenced by solutions and time (A: 9.1 +/- 3.1, B: 14.8 +/- 7.5, C: 13.3 +/- 6.1 Delta E; ANOVA: p < 0.05). Conclusions: The incorporation of MUPB affects the mechanical properties of a denture base acrylic resin; however, the only significant change was observed for flexural strength and may not be critical. Color changes were slightly higher when resin containing MUPB was immersed in wine for a prolonged time; however, the difference has debatable clinical relevance. (AU)

Processo FAPESP: 08/02725-4 - Efeitos da incorporação de um monômero anti-séptico sobre a estabilidade de cor de uma resina acrílica para base de prótese
Beneficiário:Ana Paula Zanini
Linha de fomento: Bolsas no Brasil - Iniciação Científica
Processo FAPESP: 07/05245-0 - Incorporação de um monômero anti-séptico em resina acrílica para base de prótese
Beneficiário:Raphael Freitas de Souza
Linha de fomento: Auxílio à Pesquisa - Regular
Processo FAPESP: 09/06614-5 - Incorporação de um monômero anti-séptico em resina acrílica para base de prótese
Beneficiário:Maria Paula Della Vecchia
Linha de fomento: Bolsas no Brasil - Programa Capacitação - Treinamento Técnico