Fabrication of Sr- and Co-doped lanthanum chromite interconnectors for SOFC

Texto completo
Autor(es):
Setz, L. F. G. [1] ; Santacruz, I. [2] ; Colomer, M. T. [3] ; Mello-Castanho, S. R. H. ; Moreno, R. [3]
Número total de Autores: 5
Afiliação do(s) autor(es):
[1] Univ Fed Sao Carlos DEMa UFSCar, Dept Mat Engn, Sao Carlos, SP - Brazil
[2] Univ Malaga, Dept Quim Inorgan Cristalog & Mineral, E-29071 Malaga - Spain
[3] ICV CSIC, Inst Ceram & Vidrio, Madrid 28049 - Spain
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: Materials Research Bulletin; v. 46, n. 7, p. 983-986, JUL 2011.
Citações Web of Science: 8
Resumo

Many studies have been performed dealing with the processing conditions of electrodes and electrolytes in solid oxide fuel cells (SOFCs). However, the processing of the interconnector material has received less attention. Lanthanum chromite (LaCrO(3)) is probably the most studied material as SOFCs interconnector. This paper deals with the rheology and casting behaviour of lanthanum chromite based materials to produce interconnectors for SOFCs. A powder with the composition La(0.80)Sr(0.20)Cr(0.92)CO(0).(08)O(3) was obtained by combustion synthesis. Aqueous suspensions were prepared to solids loading ranging from 8 to 17.5 vol.%, using ammonium polyacrylate (PAA) as dispersant and tetramethylammonium hydroxide (TMAH) to assure a basic pH and providing stabilization. The influence of the additives concentrations and suspension ball milling time were studied. Suspensions prepared with 24 h ball milling, with 3 wt.% and 1 wt.% of PAA and TMAH, respectively, yielded the best conditions for successful slip casting. Sintering of the green discs was performed in air at 1600 degrees C for 4 h leading to relatively dense materials. (C) 2011 Elsevier Ltd. All rights reserved. (AU)