Comparative study of the tribological behavior under hybrid lubrication of diamond-like carbon films with different adhesion interfaces

Texto completo
Autor(es):
Costa, R. P. C. [1] ; Lima-Oliveira, D. A. [2] ; Marciano, F. R. [3] ; Lobo, A. O. [3] ; Corat, E. J. [1] ; Trava-Airoldi, V. J. [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Inst Nacl Pesquisas Espaciais INPE, Associated Lab Sensors & Mat, BR-12227010 Sao Jose Dos Campos, SP - Brazil
[2] Clorovale Diamantes Ind & Comercio Ltda, BR-12229390 Sao Jose Dos Campos, SP - Brazil
[3] Univ Vale Paraiba Univap, Lab Biomed Nanotechnol NanoBio, BR-12244000 Sao Jose Dos Campos, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: Applied Surface Science; v. 285, n. B, p. 645-648, NOV 15 2013.
Citações Web of Science: 6
Resumo

This paper reports the influence of the adhesion interlayer between stainless steel and diamond-like carbon (DLC) films in two different contact conditions: in dry air and deionized water. The water was the liquid used to understand the mechanism and chemical reactions of the tribolayer formation under boundary lubrication. The effect of silicon and carbonitride adhesion interlayer was investigated on uncoated and coated DLC films. The results show that DLC/DLC pairs using carbonitride in air (30% RH) showed 60% less friction coefficient and wear less than three orders of magnitude than DLC/DLC pairs using silicon as interlayer. In deionized water, DLC/DLC pairs using carbonitride as interlayer showed 31% less friction coefficient when compared to DLC/DLC pairs with silicon. Raman related the chemical and structural changes in the DLC films during sliding in air and in the presence of water. Scratch tests showed a critical load of 14 N and 33 N in DLC films with silicon and carbonitride, respectively. (C) 2013 Elsevier B.V. All rights reserved. (AU)

Processo FAPESP: 11/20345-7 - Estudo de filmes de carbono-tipo diamante contendo nanopartículas incorporadas para aplicações biomédicas
Beneficiário:Fernanda Roberta Marciano
Linha de fomento: Auxílio à Pesquisa - Apoio a Jovens Pesquisadores
Processo FAPESP: 11/17877-7 - Desenvolvimento de novos scaffolds poliméricos por eletrofiação com incorporação de nanotubos alinhados e nanohidroxiapatita para regeneração óssea
Beneficiário:Anderson de Oliveira Lobo
Linha de fomento: Auxílio à Pesquisa - Apoio a Jovens Pesquisadores