Texto completo
Autor(es):
da Silva, L. N. Lindolfo [1] ; Torquato, Alisson [1] ; de Assis Jr, I. Nunes ; Dousti, M. Reza [2]
Número total de Autores: 4
Afiliação do(s) autor(es):
[1] Univ Fed Rural Pernambuco UFRPE, Grp Opt Mat Funcionais, Unidade Acad Cabo de Santo Agostinho UACSA, Cabo De Santo Agostinho, PE - Brazil
[2] de Assis Jr, Jr., I. Nunes, Univ Fed Rural Pernambuco UFRPE, Grp Opt Mat Funcionais, Unidade Acad Cabo de Santo Agostinho UACSA, Cabo De Santo Agostinho, PE - Brazil
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: SOLID STATE SCIENCES; v. 112, FEB 2021.
Citações Web of Science: 0
Resumo

Er3+-doped zinc tellurite glass and glass-ceramic are prepared by simple melt-quenching technique and subsequent heat-treatments at two defined crystallization temperatures. The heat-treated sample at 460 degrees C converts to an opaque glass-ceramic with the formation of mainly Zn2Te3O8 and TeO2 crystalline phases. There is no peak observed corresponding to the ZnTeO3 phase. The effective bandwidth of the near-infrared emission band of Er3+ ions at around 1.5 mu m increases from 65 nm to 89 nm after exposing the sample to heat-treatment owing to the formation of different symmetry sites around Er3+ ions. The lifetime of this band decreases from 2.49 to 1.72 ms. The upconversion emission bands in ceramized sample show a red-shift, while the green to red upconversion intensity ratio decreases from 3 to 0.6, respectively, for glass and glass-ceramic samples. The mechanism behind this observation is discussed by possible energy transfer between Er3+ ions in the crystalline phase. (AU)