Magnetoelectric coupling at room temperature in LaTiO3/ SrTiO3 heterojunctions

Texto completo
Autor(es):
Simoes, A. Z. ; Ortega, P. P. ; Ramirez, M. A. ; Moreno, H. ; Aldao, C. M. ; Ponce, M. A. ; Moura, F.
Número total de Autores: 7
Tipo de documento: Artigo Científico
Fonte: Materials Research Bulletin; v. 162, p. 8-pg., 2023-01-30.
Resumo

This work focuses on LaTiO3 (LTO) thin films synthesized by the polymeric precursor method and deposited onto SrTiO3 (STO) substrates via spin coating. The results show interesting coexisting ferromagnetic (Mr approximate to 2.85 emu/g) - ferroelectric (Pr approximate to 18.5 mu C/cm2) responses at room temperature. Magnetoelectric coupling can be observed under DC bias magnetic field (14 V/cm.Oe), and its dielectric constant is affected by the coupling between magnetic and electric dipoles at room temperature as well as oxygen octahedra distortion along direction a. Little film-substrate mismatch significantly influences the system dielectric properties. Our results suggest the possibility to induce ferromagnetic/ferroelectric phases in the LTO/STO heterojunctions using an electric/magnetic field, respectively, due to the magnetoelectric coupling. This study also helps comprehend oxygen vacancy dynamics when applying a tensile strain or an external electric field, which is fundamental for actuators, switches, magnetic field sensors, and new types of electronic memory devices. (AU)

Processo FAPESP: 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais
Beneficiário:Elson Longo da Silva
Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs
Processo FAPESP: 19/07413-5 - Novas tendências visando aplicações de filmes finos de óxidos complexos em memórias correlacionadas por elétrons
Beneficiário:Alexandre Zirpoli Simões
Modalidade de apoio: Bolsas no Exterior - Pesquisa
Processo FAPESP: 18/18236-4 - Desenvolvimento de cerâmicas avançadas à base de CaCu3Ti4O12 na forma de pós, bulks e filmes nanoestruturados: um estudo integrado das propriedades multifuncionais
Beneficiário:Henrique Piccoli Moreno
Modalidade de apoio: Bolsas no Brasil - Doutorado Direto