Enhanced energy-storage density of BaTi0.95Zr0.05O3 via generation of defect dipoles upon lithium-doping

Autor(es)

Alkathy, Mahmoud S. ; Rahaman, Attaur ; Mastelaro, Valmor R. ; Milton, Flavio Paulo ; Zabotto, Fabio L. ; Lente, Manuel H. ; Strabello, Alexandre ; Eiras, J. A.

• Tipo de documento: Artigo Científico
• Fonte: Materials Chemistry and Physics; v. 294, p. 12-pg., 2023-01-15.

Resumo

Researchers seek the most optimal solutions to a worsening crisis and escalating energy demand. In light of this, ferroelectric (FE) ceramics have become increasingly important. In perovskite oxides, defect dipoles can significantly influence the dynamics of oxygen vacancies. The lithium ions were selected as acceptor ions doped Ba site of BaTi0.95Zr0.05O3 (BZT) based ceramics. A systematic investigation of its effect on the structural, dielectric, ferroelectric, and energy storage properties has been conducted. This study shows how to improve the energy storage density and efficiency by creating defect dipoles on the (BZT) host lattice. The obtained results indicate that Li-doping plays an essential role in changing the shape of hysteresis loops. Pinched hysteresis loops with high maximum polarization and small remnant polarization were acquired when the doping content was raised due to increasing the defect dipoles. Following the onset of defect dipoles induced by acceptor ions, the recoverable energy density increased from 0.191 J/ cm3 to 0.701 J/cm3. In contrast, the energy storage efficiency increased 12th times compared to pure one, i.e., from 7% to 81%. The BLZT0.08 sample is also exceptionally stable over a range of temperatures and frequencies, making them a good candidate for applications in the field of energy storage. Improving energy storage density and efficiency by inducing defect dipoles in ferroelectric host-lattice may be one of the attractive approaches to developing ferroelectric materials for energy storage applications. (AU)

• Processo FAPESP: 19/03110-8 - Síntese e caracterização fotovoltaica de filmes finos à base de perovskitas ferroelétricas e multiferróicas para aplicação em células solares
• Beneficiário: Mahmoud Saleh Mohammed Alkathy
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 22/00821-3 - Estrutura e propriedades elétricas de domínios em materiais multiferroicos e ferroelétricos
• Beneficiário: Attaur Rahman
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 17/13769-1 - Materiais multiferróicos e ferroelétricos para conversores de energia: síntese, propriedades, fenomenologia e aplicações
• Beneficiário: José Antonio Eiras
• Modalidade de apoio: Auxílio à Pesquisa - Temático