Bomio, M. R. D.
;
Lavela, P.
;
Santiago, A. A. G.
;
Motta, F. V.
;
Tirado, J. L.
Número total de Autores: 5
|
| Tipo de documento: | Artigo Científico |
| Fonte: | CERAMICS INTERNATIONAL; v. 49, n. 8, p. 10-pg., 2023-03-07. |
| Resumo | |
Microwave calcination is proposed as an alternative route to conventional heating to prepare layered P2-Na2/ 3Ni1/3Mn2/3O2 as a positive electrode for sodium-ion batteries. The sample obtained by the fastest conditions, with a heating ramp of 20 degrees C min-1 for only 2 h, showed well-crystallized rounded particles. Cyclic voltammetry and impedance spectroscopy evidenced a low internal cell resistance, and high diffusion coefficients, which justify its capability to sustain the highest capacity at 1 C and retain the discharge capacity for at least two hundred cycles. (AU) | |
| Processo FAPESP: | 08/57872-1 - Instituto Nacional de Ciências dos Materiais em Nanotecnologia |
| Beneficiário: | Elson Longo da Silva |
| Modalidade de apoio: | Auxílio à Pesquisa - Temático |
| Processo FAPESP: | 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais |
| Beneficiário: | Elson Longo da Silva |
| Modalidade de apoio: | Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs |