Performance of 3Y-TZP Bioceramics Under Cyclic Fatigue Loading

Autor(es)

Souza, Renato Chaves ; dos Santos, Claudinei ; Ribeiro Barboza, Miguel Justino ; Reis Pereira Baptista, Carlos Antonio ; Strecker, Kurt ; Elias, Carlos Nelson

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 11, n. 1, p. 4-pg., 2008-01-01.

Resumo

In this work, the static mechanical properties and cyclic fatigue life of 3 mol. (%) Y2O3-stabilized tetragonal zirconia polycrystalline (3Y-TZP) ceramics were investigated. Pre-sintered samples were sintered in air at 1600 degrees C for 120 minutes, and characterized by X ray diffraction and scanning electronic microscopy. Hardness and fracture toughness were determined by Vicker's indentation method, and Modulus of Rupture was determined by four-point bending testing. Fully dense sintered samples, near to 100% of theoretical density, presented hardness, fracture toughness and bending strength of 13.5 GPa, 8.2 MPa.m(1/2) and 880 MPa, respectively. The cyclic fatigue tests were also realized using four-point bending testing, within a frequency of 25 Hz and stress ratio R of 0.1. The increasing of load stress lead to decreasing of the number of cycles and the run-out specimens number. The tetragonal-monoclinic (t-m) ZrO2-transformation observed by X ray diffraction contributes to the increasing of the fatigue life. The 3Y-TZP samples clearly presents a range of loading conditions where cyclic fatigue can be detected. (AU)

• Processo FAPESP: 04/04386-1 - Desenvolvimento e caracterização de pilares cerâmicos biocompatíveis à base de compósitos Zr02-Al2O3
• Beneficiário: Claudinei dos Santos
• Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
• Processo FAPESP: 05/52971-3 - Fadiga cíclica de cerâmicas biocompatíveis a base de compósitos ZrO2/Al2O3
• Beneficiário: Renato Chaves Souza
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado