Electrical and microstructural properties of Yb-doped CeO2

Autor(es)

Matovic, B. ; Stojmenovic, M. ; Pantic, J. ; Varela, A. ; Zunic, M. ; Jiraborvornpongsa, N. ; Yano, T.

• Tipo de documento: Artigo Científico
• Fonte: JOURNAL OF ASIAN CERAMIC SOCIETIES; v. 2, n. 2, p. 6-pg., 2014-06-01.

Resumo

Nanopowdered Ce1-xYbxO2-delta solid solutions (0 <= x <= 0.2) were synthesized by a self -propagating room temperature synthesis. XRD and SEM were used to study the properties of these materials as well as the Yb solubility in CeO2 lattice. Results showed that all the obtained powders were solid solutions with a fluorite type crystal structure and with nanometric particle size. The average size of Ce1-xYbxO2-delta particles was approximately 3 nm. Electrochemical impedance spectroscopy for the sintered pellets depicted that it was possible to separate R-buik and R-gb in the temperature interval of 550-800 degrees C. The activation energy for the bulk conduction was 1.03 eV and for grain boundary conduction was 1.14 eV. Grain boundary resistivity dominates over the other resistivities. These measurements confirmed that Yb3+-doped CeO2 material had a potential as electrolyte for intermediate-temperature solid oxide fuel cell applications. (C) 2014 The Ceramic Society of Japan and the Korean Ceramic Society. Production and hosting by Elsevier B.V. All rights reserved. (AU)

• Processo FAPESP: 10/20574-3 - Filmes de Eletrólitos Baseados em Condutores de Protons em Altas Temperaturas para Aplicação em IT-SOFCs
• Beneficiário: Milan Zunic
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado