Structural behavior of secondary-bonded composite joints subjected to Mode II fatigue induced delamination

Autor(es)

Garpelli, F. P. ; Ramirez, F. M. G. ; Resende, H. B. ; Donadon, M., V ; IOP

• Tipo de documento: Artigo Científico
• Fonte: 9TH WORLD CONGRESS ON COMPUTATIONAL MECHANICS AND 4TH ASIAN PACIFIC CONGRESS ON COMPUTATIONAL MECHANICS; v. 388, p. 7-pg., 2018-01-01.

Resumo

This paper analyses the Mode II fatigue delamination growth onset for secondary bonded joints compared to co-cured joints. The materials used were composed by two carbon fiber reinforced sub-laminates joined by the secondary bonded and co-cured (without adhesive) methods. Mode II fatigue tests were performed using three-point bending End Notched Flexure test setup. The tests were performed under displacement control and a sinusoidal displacement applied at a frequency of 5 Hz with a R-d = 0.1, that mean, delta(min) = 0.1 delta(max). The main objective of this study was to obtain the strain energy release rate (SEER) versus number of cycles (N-f) in order to evaluate the effect of the adhesive on fatigue life of bonded joints. A Closed form solution for 3-ENF setup was used in order to define the displacement amplitudes that were applied in the fatigue test. The results show that the use of adhesive causes a reduction on Mode II fatigue delamination growth onset SERR (G(th)) for secondary-bonded compared to cocured joints. Finally, a scanning electron microscopy (SEM) was used to analyze the fracture surfaces of the Mode II secondary bonded specimens. The fractography images show no crack growth for the specimens tested below or at G(th) loading levels, which indicated that the value corresponds to the threshold. (AU)

• Processo FAPESP: 15/16733-2 - Modelagem de Junções Coladas para Aplicações em Estruturas Aeronáuticas de Materiais Compósitos
• Beneficiário: Mariano Andrés Arbelo
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado