Interface excess on Li2O-doped gamma-Al2O3 nanoparticles

Autor(es)

de Oliveira, Raphael A. M. P. ; da Silva, Andre L. ; Caliman, Lorena B. ; Gouvea, Douglas

• Tipo de documento: Artigo Científico
• Fonte: CERAMICS INTERNATIONAL; v. 46, n. 8, p. 6-pg., 2020-06-01.

Resumo

One of the attempts to improve gamma-alumina catalytic performance lies in the use of additives that prone to segregate on its interfaces. The catalytic activity depends on the acidity or basicity of the doping oxides. Li2O is one of these oxides that when is loaded on gamma-alumina surface decreases the number of Lewis acid sites. However, little is known about the Li2O distribution in the gamma-alumina structure and interfaces. Thus, a detailed study of the lithium oxide distribution in the nanostructure of gamma-alumina is the aim of this study. Nanometric powders were synthesized by the polymeric precursor method. The nanopowders were doped with Li+ ions (0.1, 0.5, 1, 3, 5, and 10 mol%) followed by calcination at 650 degrees C and 750 degrees C for 15 h. The powders were characterized by XRD, XRF, FTIR-DRIFT, BET specific surface area (SSA) and helium pycnometry. The surface excess due to the lithium oxide segregation was determined by the selective lixiviation method which has proved to be effective in quantifying surface excess of segregated ions at oxide interfaces. The crystallite sizes of the nanopowders varied from 3.3 nm to 9.2 nm, while their SSA were between 82.0 m(2)/g to 119.9 m(2)/g. The chemical analyses suggest that the lithium segregates in the gamma-alumina interfaces at 650 degrees C, but it volatilizes from the surface after calcination at 750 degrees C. (AU)

• Processo FAPESP: 13/23209-2 - Segregação de íons na superfície de nano-óxidos e sua influência no processo coloidal
• Beneficiário: Douglas Gouvêa
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 15/50443-1 - Interfaces in ceramic processing
• Beneficiário: Douglas Gouvêa
• Modalidade de apoio: Auxílio à Pesquisa - Regular