Improving laser performance at 1081 nm in Yb3+-doped tellurite glasses with low threshold

Autor(es)

Lozano, C. G. ; dos Santos, J. F. M. ; Merizio, L. G. ; de Oliveira Jr, M. ; Messaddeq, Y. ; Marega Jr, E. ; Rivera, V. A. G.

• Tipo de documento: Artigo Científico
• Fonte: Materials Research Bulletin; v. 189, p. 7-pg., 2025-09-01.

Resumo

Yb3+-doped glass lasers have promising applications in optical telecommunications, industrial processing, due to their broad or short emission and gain bandwidth, as well as their cost-effective maintenance and compact design. This research reports the laser operation of Yb3+-doped tellurite glass emitting at 1081 nm and evaluates its performance under varying pump powers using a continuous-wave diode laser at 976 nm, with a bandwidth of 20 nm. Our findings reveal that the glasses do not exhibit the formation of Yb3+ clusters. The laser efficiency increased from 1.7 % to 5.5 % as the concentration of Yb3+ ions was raised to 0.9 mol %, although quenching of the emission intensity at higher concentrations. The laser threshold was determined at a pump power of 120 mW, with the glasses showing good thermal stability without damage. These glasses offer new opportunities for applications in optical telecommunications, particularly in Ytterbium-Erbium-doped fibre amplifier systems as a pumping source. (AU)

• Processo FAPESP: 20/04835-3 - Controlando o estado de polarização da emissão de terras raras em vidros teluritos a partir de nano-antenas plasmônicas
• Beneficiário: Gaston Lozano Calderón
• Modalidade de apoio: Bolsas no Brasil - Doutorado
• Processo FAPESP: 13/07276-1 - CEPOF - Centro de Pesquisa em Óptica e Fotônica
• Beneficiário: Vanderlei Salvador Bagnato
• Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs
• Processo FAPESP: 22/05478-5 - Controlando o estado de polarização da emissão de terras raras em vidros teluritos a partir de nano-antenas plasmônicas
• Beneficiário: Gaston Lozano Calderón
• Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Doutorado
• Processo FAPESP: 23/11979-0 - Interação luz-matéria em metasuperfícies plasmônicas de nanovidros luminescentes: caracterização espectroscópica e fototérmica
• Beneficiário: Jéssica Fabiana Mariano dos Santos
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado