| Fonte: | TEXTILES; v. 5, n. 4, p. 19-pg., 2025-12-18. |
| Resumo | |
Textile-reinforced concrete (TRC) is an alternative class of mechanical reinforcement for cement composites. The biaxial braided reinforcement structure in composite materials with diverse cross-sectional shapes offers high adaptability, torsional stability, and resistance to damage. In general, 3D textile reinforcements improve the mechanical properties of composites compared to 2D reinforcements. This study aimed to verify reinforcement behavior by comparing multidimensional braided textiles, 2D (one- and two-layer) reinforcements, and 3D reinforcement in composite cementitious boards. Experimental tests were performed to evaluate the effect of textile structures on cementitious composites using four-point bending tests, porosity measurements, and crack patterns. All textiles showed sufficient space between yarns, allowing the matrix (a commercial formulation) to infiltrate and influence the composite mechanical properties. All composites presented ductility behavior. The two layers of 2D textile composites displayed thicker cracks, influenced by shear forces. Three-dimensional textiles exhibited superior values in four-point bending tests for modulus of rupture (7.4 +/- 0.5 MPa) and specific energy (5.7 +/- 0.3 kJ/m2). No delamination or debonding failure was observed in the boards after the bending tests. The 3D textile structure offers a larger contact area with the cementitious matrix and creates a continuous network, enabling more uniform force distribution in all directions. (AU) | |
| Processo FAPESP: | 21/04780-7 - Estudo da durabilidade em compósitos cimentícios reforçados com fibras lignocelulósicas com matrizes com MgO e MgSO4 |
| Beneficiário: | Adriano Galvão de Souza Azevedo |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |
| Processo FAPESP: | 24/02445-4 - Uso de Sementes de Nucleação no Aumento da Captura e Mineralização do CO2 Proveniente da Indústria Sucroalcooleira em Fibrocimentos Low-Carb |
| Beneficiário: | Adriano Galvão de Souza Azevedo |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |
| Processo FAPESP: | 25/27072-9 - Instituto de Inovação em Materiais Cimentícios Ecoeficientes para Descarbonização da Construção - IMCEDC |
| Beneficiário: | Holmer Savastano Junior |
| Modalidade de apoio: | Auxílio à Pesquisa - Temático |
| Processo FAPESP: | 22/07179-5 - Avaliação da durabilidade de fibrocimentos de matriz MOS reforçados com fibras lignocelulósicas e submetidos à processos de carbonatação acelerada |
| Beneficiário: | Adriano Galvão de Souza Azevedo |
| Modalidade de apoio: | Bolsas no Exterior - Estágio de Pesquisa - Pós-Doutorado |
| Processo FAPESP: | 14/50948-3 - INCT 2014: tecnologias ecoeficientes avançadas em produtos cimentícios |
| Beneficiário: | VANDERLEY MOACYR JOHN |
| Modalidade de apoio: | Auxílio à Pesquisa - Temático |