Nafion-TiO2 hybrid electrolytes for stable operation of PEM fuel cells at high temperature

Texto completo
Autor(es):
Santiago, E. I. [1] ; Isidoro, R. A. [1] ; Dresch, M. A. [1] ; Matos, B. R. [1] ; Linardi, M. [1] ; Fonseca, F. C. [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] IPEN CNEN SP, BR-05508000 Sao Paulo - Brazil
Número total de Afiliações: 1
Tipo de documento: Artigo Científico
Fonte: Electrochimica Acta; v. 54, n. 16, p. 4111-4117, JUN 30 2009.
Citações Web of Science: 68
Resumo

The fabrication and characterization of Nafion-TiO(2) hybrid electrolytes for proton exchange membrane fuel cell (PEMFC) operating at high temperature are reported. A low temperature sol-gel synthesis, based on the formation of a sol from Ti-peroxy complex, was used to effectively incorporate hydrophilic anatase TiO(2) nanoparticles into the Nafion matrix. Fuel cell testing at temperatures up to 130 degrees C revealed that the hybrid membranes exhibit an increasing ohmic drop with increasing TiO(2) content incorporated into the polymer. However, at high temperatures and low relative humidity (RH) the performance of fuel cells using the hybrid electrolytes was found to surpass the one of Nafion. Electrochemical impedance spectroscopy (EIS) measurements suggest that enhancement of the fuel cell performance at high temperature and low RH is related to a reduced polarization resistance, indicating that the hybrid electrolytes contribute for a better water management of the system. In addition, it was found that the inorganic phase confers stability to the polymer, allowing for the operation at high temperature and reduced RH. (C) 2009 Elsevier Ltd. All rights reserved. (AU)

Processo FAPESP: 04/04555-8 - Síntese e caracterização de nanocompósitos nafion-óxidos higroscópicos para aplicação como membranas auto-umidificadas em células a combustível de membrana de troca protônica de temperatura intermediária
Beneficiário:Elisabete Inacio Santiago
Linha de fomento: Auxílio à Pesquisa - Apoio a Jovens Pesquisadores
Processo FAPESP: 02/01131-7 - Alteracoes estruturais em nanoparticulas de semicondutores para melhor aproveitamento da radiacao solar em processos de fotodegradacao.
Beneficiário:Jorge Moreira Vaz
Linha de fomento: Auxílio à Pesquisa - Regular