Nanoscale investigation of ferroelectric and piezoelectric properties in (Pb,Ca)TiO3 thin films grown on LaNiO3/LaAlO3(100) and Pt/Si(111) using piezoresponse force microscopy

Texto completo
Autor(es):
Capeli, R. A. ; Pontes, F. M. ; Pontes, D. S. L. ; Chiquito, A. J. ; Bastos, W. B. ; Pereira-da-Silva, Marcelo A. ; Longo, E.
Número total de Autores: 7
Tipo de documento: Artigo Científico
Fonte: Materials Letters; v. 196, p. 64-68, JUN 1 2017.
Citações Web of Science: 1
Resumo

Single phase polycrystalline and strong textured Pb0.76Ca0.24TiO3 (PCT24) thin films have been grown on platinum coated silicon and LaAlO3(100) (LAO) substrates using LaNiO3 (LNO) as a buffer layer by chemical solution deposition. X-ray diffraction measurements showed that the PCT24 thin films crystallize in a highly a-oriented single phase on LNO/LAO(100). The effects of the LNO buffer layer, nature of the substrate, and film orientation on the ferroelectric and piezoelectric properties were investigated in the nanoscale range using piezoresponse force microscopy (PFM). Local piezoelectric hysteresis loops for PCT24/LNO/LAO(100) oriented films and PCT24/Pt/Si polycrystalline films were measured on selected grains. From these piezoloops, PCT24/LNO/LAO(100) oriented films show a higher response (maximum relative d33 value) than PCT24/Pt/Si polycrystalline films. Furthermore, the comparison of simultaneously acquired surface morphology and piezoresponse images of the PCT24/Pt/Si films revealed the presence of inactive grain regions. In contrast, highly a-oriented films showed a higher presence of active grains. Our observations suggest that the improvement of ferro/piezoelectric properties is greatly associated with the use of LNO buffer layers and the growth of highly a-oriented films. (C) 2017 Elsevier B. V. All rights reserved. (AU)

Processo FAPESP: 11/20536-7 - Materiais ferroelétricos multifuncionais: estudos das propriedades ópticas, elétricas e fotoluminescente
Beneficiário:Debora da Silva Lima Pontes
Linha de fomento: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais
Beneficiário:Elson Longo da Silva
Linha de fomento: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs
Processo FAPESP: 12/14106-2 - Designe de óxidos multifuncionais com arquitetura perovskite (Pb,Sr,La, Bi) (Ti,Fe) O3
Beneficiário:Fenelon Martinho Lima Pontes
Linha de fomento: Auxílio à Pesquisa - Regular