Influence of Particle and Air-Abrasion Moment on Y-TZP Surface Characterization and Bond Strength

Autor(es)

Martins, Samira Branco ^[1] ; Abi-Rached, Filipe de Oliveira ^[1] ; Adabo, Gelson Luis ^[1] ; Baldissara, Paolo ^[2] ; Fonseca, Renata Garcia ^[1]

Afiliação do(s) autor(es)

^[1] Univ Estadual Paulista, Araraquara Dent Sch, Dept Dent Mat & Prosthodont, Sao Paulo - Brazil

^[2] Alma Mater Studiorum Univ Bologna, Dept Oral Sci, Bologna - Italy

• Tipo de documento: Artigo Científico
• Fonte: JOURNAL OF PROSTHODONTICS-IMPLANT ESTHETIC AND RECONSTRUCTIVE DENTISTRY; v. 28, n. 1, p. E271-E278, JAN 2019.
• Citações Web of Science: 1

Resumo

Purpose To evaluate the influence of particle and air-abrasion on the surface characterization and shear bond strength (SBS) of a Y-TZP ceramic with a resin cement. Materials and Methods Y-TZP specimens were air-abraded with 50 mu m alumina particles; 120 mu m alumina particles; 30 mu m silica-coated alumina particles (Rocatec Soft); 110 mu m silica-coated alumina particles (Rocatec Plus). Air-abrasion was performed before (BS); after (AS); before and after (BAS) zirconia sintering. Surface characterization included roughness (n = 10), wettability (n = 10), morphology (n = 2), and elemental composition (n = 2). For SBS (n = 11), composite resin discs were bonded to the air-abraded and silane-treated zirconia surface, with the resin cement RelyX ARC. Failure mode was determined. Roughness, wettability, and SBS data were analyzed by two-way ANOVA with pairwise interaction and Tukey's test (alpha = 0.05). Results Air-abrasion performed with coarser particles at BS and BAS moments provided the highest roughness values, while the lowest roughness values were observed with particles combined with AS moment (p < 0.01). Rocatec Plus provided lower contact angle than the 120 mu m alumina particles (p = 0.013), and BAS exhibited lower contact angle than BS (p = 0.002). The combinations 120 mu m/BS and the silica-coated alumina particles/AS and /BAS showed the highest SBS (p < 0.05). The combination of each particle/BAS was statistically similar to the same particle/AS. Failure mode was 100% adhesive for all groups. The interaction particle size/air-abrasion moment determined the morphological pattern. Silicon was observed only in the Rocatec groups. Conclusions Roughness was influenced by the particle size and was higher when the zirconia was air-abraded in its green stage. The particle composition played an important role in the wettability and both studied air-abrasion moments provided similar wettability than the one in which air-abrasion is usually performed. The highest SBS values were observed in the three moments, by using certain particles for each moment. (AU)

• Processo FAPESP: 12/08534-1 - Avaliação da influência do tamanho de partícula e do momento do jateamento na caracterização superficial (composição, morfologia, molhamento e rugosidade) da zircônia e na resistência de união com cimento resinoso