Interlaminar crack onset in co-cured and co-bonded composite joints under mode I cyclic loading

Texto completo
Autor(es):
Shiino, Marcos Yutaka [1] ; Gonzalez Ramirez, Francis Mariana [2] ; Garpelli, Felipe Parise [2] ; Alves da Silveira, Nubia Nale [2] ; Mendonca Sales, Rita de Cassia [2, 3] ; Donadon, Mauricio Vicente [2]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Univ Estadual Paulista Unesp, Dept Engn Ambiental, Inst Ciencia & Tecnol, BR-12247004 Sao Jose Dos Campos - Brazil
[2] Inst Tecnol Aeronaut ITA, Div Engn Aeronaut, Praca Marechal do Ar Eduardo Gomes, BR-12228900 Sao Jose Dos Campos, SP - Brazil
[3] Fac Tecnol Sao Jose dos Campos Prof Jessen Vidal, Sao Jose Dos Campos, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES; v. 42, n. 3, p. 752-763, MAR 2019.
Citações Web of Science: 0
Resumo

Composite joints exhibit different behavior in regard to delamination resistance when dealing with fatigue phenomenon. This research work focuses on an investigation to understand the failure mechanisms on the interfacial strength domain for delamination onset in cocured and cobonded joints. The analysis was based on strain energy release rate versus number of cycles plots that were obtained from fatigue tests in mode I with a stress ratio R = 0.1. The analysis encompassed from the microscopic to mesoscopic level obtained from scanning electron microscopic, and the images processed to extract the most relevant fracture patterns. The main difference between the two technologies was the stress concentration at the crack tip in which the cobonded joint presents a fabric carrier that blunts the adhesive layer, then delaying the delamination. This paper provides important information and guidelines to aid designers in the selection of the best composite joint for high-performance structural applications. (AU)

Processo FAPESP: 11/01937-0 - Taxa de delaminação em compósitos 5HS carbono/epóxi processado via RTM: relação do carregamento axial tração-tração como modos I e II puros
Beneficiário:Marcos Yutaka Shiino
Modalidade de apoio: Bolsas no Brasil - Doutorado
Processo FAPESP: 12/07646-0 - Avaliação do efeito do gradiente de pressão no processamento RTM em laminado 5HS por DCB no modo i em fadiga
Beneficiário:Marcos Yutaka Shiino
Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Doutorado
Processo FAPESP: 15/16733-2 - Modelagem de Junções Coladas para Aplicações em Estruturas Aeronáuticas de Materiais Compósitos
Beneficiário:Mariano Andrés Arbelo
Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado