Influence of the spark-plasma texturing conditions on the intragranular features of Bi-2223 ceramic samples

Texto completo
Autor(es):
Perez-Acosta, L. [1] ; Govea-Alcaide, E. [2, 3] ; Rosales-Saiz, F. [3] ; Noudem, J. G. [4] ; Machado, I. F. [5] ; Jardim, R. F. [6]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Univ Camaguey, Fac Informat & Ciencias Exactas, Dept Fis, Camaguey - Cuba
[2] Univ Fed Amazonas, Dept Fis, Manaus, Amazonas - Brazil
[3] Univ Granma, Fac Ciencias Informat Nat & Exactas, Dept Matemat Fis, Bayamo - Cuba
[4] Normandie Univ, ENSICAEN, UNICAEN, CNRS, CRISMAT, F-14000 Caen - France
[5] Univ Sao Paulo, Escola Politecn, Dept Engn Mecatron & Sistemas Mecan, Sao Paulo, SP - Brazil
[6] Univ Sao Paulo, Inst Fis, Dept Fis & Mat Mecan, Sao Paulo - Brazil
Número total de Afiliações: 6
Tipo de documento: Artigo Científico
Fonte: JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS; v. 30, n. 7, p. 6984-6992, APR 2019.
Citações Web of Science: 0
Resumo

The influence of the spark-plasma texturing (SPT) conditions on the intragranular superconducting properties of Bi1.65Pb0.35Sr2Ca2Cu3O10+ (Bi-2223) samples has been investigated. Also, the SPT samples were subjected to a post-annealing heat treatments (PAHT) in different times. Intragranular superconducting features, extracted from magnetoresistance measurements, (T,H), in applied magnetic fields up to 9 T, were studied by analyzing the temperature dependence of the in-plane upper critical field, Hc2ab(T), and the magnetic field dependence of the pinning energy at zero temperature, U(0,H). The results indicated that, before and after the PAHT, values of the Hc2ab(0), obtained by using the Werthamer-Helfand-Hohenberg formula, increased approximate to 21%, i.e., from 115.8 to 140.2 T. We have also found that the effective intragranular pinning energy at zero applied magnetic field, U0=U(0,0), also increased over approximately three times, from 0.28 to 0.98 eV. These results strong strongly indicate that the SPT process is responsible for inducing deoxygenation at the intragranular level of ceramic samples, a feature presumably occurring near of the end of planar defects. (AU)

Processo FAPESP: 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais
Beneficiário:Elson Longo da Silva
Linha de fomento: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs
Processo FAPESP: 13/20181-0 - Evolução do comportamento isolante Kondo topológico em Sm1xRxB6 (r = Sr, Yb)
Beneficiário:Priscila Ferrari Silveira Rosa
Linha de fomento: Bolsas no Exterior - Estágio de Pesquisa - Pós-Doutorado
Processo FAPESP: 14/19245-6 - Procura por novos materiais supercondutores
Beneficiário:Renato de Figueiredo Jardim
Linha de fomento: Bolsas no Exterior - Pesquisa