Sintering of translucent and single-phase nanostructured scandia-stabilized zirconia

Autor(es)

Grosso, Robson L. ^{[1, 2, 3, 4]} ; Muche, Dereck N. F. ^{[1, 2]} ; Yonamine, Taeko ^[5] ; Muccillo, Eliana N. S. ^[4] ; Dillon, Shen J. ^[3] ; Castro, Ricardo H. R. ^{[1, 2]}

Afiliação do(s) autor(es)

^[1] Univ Calif Davis, NEAT ORU, Davis, CA 95616 - USA

^[2] Univ Calif Davis, Dept Mat Sci & Engn, Davis, CA 95616 - USA

^[3] Univ Illinois, Dept Mat Sci & Engn, Urbana, IL 61801 - USA

^[4] Energy & Nucl Res Inst, POB 11049, Sao Paulo - Brazil

^[5] Inst Technol Res, BR-05508901 Sao Paulo - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Materials Letters; v. 253, p. 246-249, OCT 15 2019.
• Citações Web of Science: 0

Resumo

Fully-dense and single-phase nanostructured scandia-stabilized zirconia specimens were produced by high-pressure spark plasma sintering technique. Nanocrystalline powders were prepared by the copre-cipitation method. Green pellets were sintered at temperatures varying from 700 to 900 degrees C and pressures from 1.4 to 2 GPa, resulting in dense microstructures with single-phase fluorite-type cubic structure within a wide range of Sc2O3 content (6-15 mol%). The average grain size of sintered specimens ranged from 8 to 20 nm. Transmittance spectra confirm translucence in sintered specimens, which is consistent with full density. The results reported here reveal that the polymorphism challenge in the zirconia-scandia system can be successfully suppressed by this consolidation technique, which allows for controlling the grain size of bulk specimens. (C) 2019 Elsevier B.V. All rights reserved. (AU)

• Processo FAPESP: 16/06205-1 - Caracterização de cerâmicas de zircônia-escândia nanoestruturadas consolidadas por sinterização assistida por campo elétrico.
• Beneficiário: Robson Lopes Grosso
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 17/25501-3 - Transição de fase dependente do tamanho de grão e relação de Hall-Petch em zircônia-escândia nanocristalina: um estudo por MET in-situ
• Beneficiário: Robson Lopes Grosso
• Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Pós-Doutorado