One-Step Synthesis of AuCu/TiO2 Catalysts for CO Preferential Oxidation

Texto completo
Autor(es):
Catarine Santos Lopes Alencar [1] ; Ana Rita Noborikawa Paiva [2] ; Julio Cesar Martins da Silva ; Jorge Moreira Vaz [4] ; Estevam Vitorio Spinacé [5]
Número total de Autores: 5
Afiliação do(s) autor(es):
[1] Instituto de Pesquisas Energéticas e Nucleares - Brasil
[2] Instituto de Pesquisas Energéticas e Nucleares - Brasil
[4] Instituto de Pesquisas Energéticas e Nucleares - Brasil
[5] Instituto de Pesquisas Energéticas e Nucleares - Brasil
Número total de Afiliações: 5
Tipo de documento: Artigo Científico
Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 23, n. 5 2020-10-23.
Resumo

Abstract Au/TiO2 (1wt% Au), Cu/TiO2 (1wt% Cu) and AuCu/TiO2 (1wt% AuCu) catalysts with different Au:Cu mass ratios were prepared in one-step synthesis using sodium borohydride as reducing agent. The resulting catalysts were characterized by X-ray diffraction (XRD), X-ray Dispersive Energy (EDX), Transmission Electron Microscopy (TEM) and Temperature Programmed Reduction (TPR) and tested for the preferential oxidation of carbon monoxide (CO-PROX reaction) in H2-rich gases. EDS analysis showed that the Au contents are close to the nominal values whereas for Cu these values are always lower. X-ray diffractograms showed only the peaks of TiO2 phase; no peaks of metallic Au and Cu species or oxides phases were observed. TPR and high-resolution TEM analysis showed that AuCu/TiO2 catalysts exhibited most of Au in the metallic form with particles sizes in the range of 3-5 nm and that Cu was found in the form of oxide in close contact with the Au nanoparticles and well spread over the TiO2 surface. The AuCu/TiO2 catalysts exhibited good performance in the range of 75-100 °C and presented a better catalytic activity when compared to the monometallic ones. A maximum CO conversion of 98.4% with a CO2 selectivity of 47% was obtained for Au0.50Cu0.50/TiO2 catalyst at 100oC. (AU)

Processo FAPESP: 14/09087-4 - Estudos sobre o uso do bioetanol em células a combustível do tipo PEMFC e SOFC
Beneficiário:Marcelo Linardi
Modalidade de apoio: Auxílio à Pesquisa - Temático
Processo FAPESP: 17/11937-4 - Rota sustentável para a conversão de metano com tecnologias eletroquímicas avançadas
Beneficiário:Fabio Coral Fonseca
Modalidade de apoio: Auxílio à Pesquisa - Programa Centros de Pesquisa em Engenharia
Processo FAPESP: 14/50279-4 - Brasil Research Centre for Gas Innovation
Beneficiário:Julio Romano Meneghini
Modalidade de apoio: Auxílio à Pesquisa - Programa Centros de Pesquisa em Engenharia