Unraveling the impact of phase separation induced by thermal annealing on shape memory effect of polyester-based thermoplastic polyurethane

Autor(es)

Flores Valim, Fernanda Cabrera ^{[1, 2]} ; Oliveira, Gustavo Peixoto ^[1] ; Vasconcelos, Gibran da Cunha ^[3] ; de Paiva, Lucilene Betega ^[2] ; Santillo, Chiara ^[4] ; Lavorgna, Marino ^[4] ; Espanhol Andrade, Ricardo Jorge ^[1]

Afiliação do(s) autor(es)

^[1] Mackenzie Presbyterian Inst, Mackgraphe Mackenzie Inst Res Graphene & Nanotech, Sao Paulo - Brazil

^[2] Inst Technol Res IPT, Lab Chem Proc & Particle Technol, Grp Bionanomfg BIONANO, Sao Paulo - Brazil

^[3] Inst Technol Res IPT, Lightweight Struct Lab LEL, Sao Paulo - Brazil

^[4] Natl Res Council Italy, Inst Polymers Composites & Biomat, I-80055 Portici - Italy

• Tipo de documento: Artigo Científico
• Fonte: Journal of Applied Polymer Science; v. 139, n. 9 OCT 2021.
• Citações Web of Science: 0

Resumo

In this study polyester-based thermoplastic polyurethane (TPU) samples were annealed at 110 degrees C for 0, 8, 16, and 24 h. To elucidate the relationship between the hard and soft phase separation and the shape memory properties, the samples were characterized within a rheometer, by selecting well defined thermal cycles. The results showed an enhancement of the shape recovery ratio (R-r similar to 65%) for all the annealed samples, when compared to the non-annealed TPU (R-r similar to 60%). This behavior was attributed to the modifications of hard-soft domain morphology occurring during the thermal annealing treatment, as it was shown both by differential scanning calorimetry with the shift in thermal transitions toward higher temperature, due the formation of new short-range ordered hard domains and infrared spectroscopy, with the increase in degree of phase separation. Analyzing small-angle X-ray scattering, the decrease of the invariant also confirmed the enhancement of short-range domains. The formation of these new short-range domains acted as crosslinking points in TPU's morphology leading to an increase in stiffness, presented by higher Young and storage modulus. Based on these results, a model mechanism is proposed to correlate the morphology and structure of the annealed materials with their shape memory effect. (AU)