Ti-13Nb-13Zr (TNZ) parts were produced by selective laser melting under an atmosphere with a relatively high O content using a comprehensive combination of laser powers and laser beam scanning velocities. The influence of processing conditions on the density, microstructure, interstitial element contents (N and O), and hardness of as-printed TNZ parts were studied. The N and O contents in the TNZ parts increased on increasing the energy density (ED). Despite the high O content in the chamber during laser processing, it was possible to obtain TNZ parts with high density and relatively low N and O contents, depending on the ED applied. Two different types of microstructure were observed in the TNZ parts: alpha ' martensite and alpha/alpha ' + beta phases. Depending on its microstructure, the TNZ parts presented interstitial solid solution hardening and second phase hardening. (AU) | |
| Processo FAPESP: | 17/20877-5 - Efeito dos parâmetros do processo de fusão seletiva a laser sobre a microestrutura de ligas Ti-13%Nb-13%Zr e Nb-47%Ti |
| Beneficiário: | Edwin Sallica Leva |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |
| Processo FAPESP: | 16/50199-6 - Obtenção de próteses ortopédicas de ligas Nb-Ti e Ti-Nb-Zr por fusão seletiva a laser |
| Beneficiário: | Fernando Jose Gomes Landgraf |
| Modalidade de apoio: | Auxílio à Pesquisa - Parceria para Inovação Tecnológica - PITE |
| Processo FAPESP: | 17/20926-6 - Estudo da hidretação, moagem e dehidretação de ligas Ti-13%Nb-13%Zr e Nb-47%Ti |
| Beneficiário: | Railson Bolsoni Falcão |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |