| Texto completo | |
| Autor(es): |
Ortiz, Eder L.
;
Osorio, Wislei R.
;
Bortolozo, Ausdinir D.
;
Padilha, Giovana S.
Número total de Autores: 4
|
| Tipo de documento: | Artigo Científico |
| Fonte: | METALS; v. 12, n. 6, p. 15-pg., 2022-06-01. |
| Resumo | |
Al and its alloys constitute one of the most versatile, economical, and attractive materials for a wide range of applications. The 7xxx and 2xxx series alloys achieve the highest mechanical strength among the aluminum alloys. In this investigation, powder metallurgy is used to characterize the microstructural and mechanical properties of a noncommercial Al6Cu5Zn alloy. Initial powder sizes are determined, and the best conditions are obtained for distribution between 75 and 106 mu m. The samples are sintered at 585 degrees C, 600 degrees C and 615 degrees C for 0.5, 1.5 h and 3 h. Similar mechanical behavior to that of the as-cast Al-Cu-based alloys is attained (similar to 125 MPa) for the samples sintered at 615 degrees C for 3 h. In terms of a reduction in energy consumption and in the metal fumes commonly evidenced by foundry applications, Al-Zn powders have the potential to be associated with Al and Cu powders in an Al6Cu5Zn composite constitution. (AU) | |
| Processo FAPESP: | 13/12729-5 - Influência da sinterização por micro-ondas em compostos nanolamidados supercondutores pertencentes à família MAX |
| Beneficiário: | Ausdinir Danilo Bortolozo |
| Modalidade de apoio: | Auxílio à Pesquisa - Regular |