Porous 8YSZ Ceramics Prepared with Alkali Halide Sacrificial Additives

Autor(es)

Diaz, Julio Cesar Camilo Albornoz ; Muccillo, Eliana Navarro dos Santos ; Muccillo, Reginaldo

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS; v. 16, n. 9, p. 11-pg., 2023-05-03.

Resumo

8 mol% Y2O3-stabilized ZrO2 (8YSZ) ceramics were prepared with KCl and LiF additions to obtain porous specimens with high skeletal density. Thermogravimetric and differential thermal analyses (TG/DTA) were carried out on 8YSZ and on 8YSZ mixed to 5 wt.% KCl or 5 wt.% LiF as sacrificial pore formers that were thermally removed during sintering. The melting and evaporation of the alkali halides were evaluated by differential thermal analysis. Dilatometric analysis was also carried out following the same TG/DTA temperature profile with results suggesting rearrangement of the 8YSZ particles during LiF and KCl melting. The dilatometric data of 8YSZ green pellets mixed to KCl or LiF exhibited an initial expansion up to the melting of the alkali halide, followed by shrinkage due to sintering evolution with grain growth and pore elimination. The time that the alkali halide molten phase was kept during sintering was found to be an important parameter for obtaining 8YSZ-sintered specimens with specific pore content; bulk density and open porosity could then be tuned by controlling the time the alkali halide remained liquid during sintering. Scanning electron microscopy images of the pellet fracture surfaces showed pores that contributed to increasing the electrical resistivity as evaluated by impedance spectroscopy analysis. (AU)

• Processo FAPESP: 20/05250-9 - Detecção da luminescência em sinterização sem pressão assistida por campo elétrico em cerâmicas de zircônia estabilizadas com itria
• Beneficiário: Reginaldo Muccillo
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 17/11937-4 - Rota sustentável para a conversão de metano com tecnologias eletroquímicas avançadas
• Beneficiário: Fabio Coral Fonseca
• Modalidade de apoio: Auxílio à Pesquisa - Programa Centros de Pesquisa em Engenharia
• Processo FAPESP: 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais
• Beneficiário: Elson Longo da Silva
• Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs