| Texto completo | |
| Autor(es): |
Bortolozo, A. D.
;
Sant'Anna, O. H.
;
dos Santos, C. A. M.
;
Machado, A. J. S.
Número total de Autores: 4
|
| Tipo de documento: | Artigo Científico |
| Fonte: | MATERIALS SCIENCE-POLAND; v. 30, n. 2, p. 6-pg., 2012-06-01. |
| Resumo | |
We report on the investigation of the Ti2GeC properties by X-ray diffraction, magnetic and electrical resistivity measurements. Polycrystalline samples of Ti2GeC with nominal compositions were prepared by solid state reaction. X-ray powder patterns suggest that all peaks can be indexed with the hexagonal phase of Cr2AlC prototype. The temperature dependence of both electrical resistivity and magnetization indicate a bulk type-II superconductivity at 9.5 K. Magnetoresistive data suggest an upper critical field of B-c2 similar to 8.1 T and coherence length similar to 61 A degrees . Furthermore, the results highlight the highest critical temperature reported up to now for an H-phase. (AU) | |
| Processo FAPESP: | 04/13267-6 - Estudo da supercondutividade em carbetos lamelares da família M2AX |
| Beneficiário: | Ausdinir Danilo Bortolozo |
| Modalidade de apoio: | Bolsas no Brasil - Doutorado Direto |
| Processo FAPESP: | 09/00610-8 - Investigação da coexistência de magnetismos e supercondutividade em novas ligas dos sistemas intersticiais Fe-Se-X e Mg-Ce-X |
| Beneficiário: | Ausdinir Danilo Bortolozo |
| Modalidade de apoio: | Auxílio à Pesquisa - Jovens Pesquisadores |