On the Phase Transformation in Mechanically Alloyed Ni-Nb and Ni-Ta and Ni-Nb-Ta Powders

Autor(es)

Ferraretto, Ana Clara ; Trindade Ramos, Erika Coaglia ; Ramos, Alfeu Saraiva ; Salgado, L ; Ambrozio, F

• Tipo de documento: Artigo Científico
• Fonte: Materials Science Forum; v. 727-728, p. 2-pg., 2012-01-01.

Resumo

This paper reports on the phase transformation during the preparation of Ni-25Nb, Ni-25Ta, Ni-20Nb-5Ta and Ni-15Nb-10Ta (at-%) powders by high-energy ball milling from elemental powders. The milling process was performed in a planetary ball milling using stainless steel balls and vials, rotary speed of 300rpm, and a ball-to-powder of 10:1. To minimize contamination and spontaneous ignition the powders were handled under argon atmosphere in a glove box. The milled powders were characterized by means of X-ray diffraction techniques. Results indicated that the Ni atoms were preferentially dissolved into the Nb (and/or Ta) lattice at the initial milling times, which contributed to change the relative intensity on the diffraction peaks. After the dissolution of Nb (and/or Ta) into the Ni lattice, the Ni peaks were moved to the direction of lower diffraction angles in Ni-25Nb, Ni-25Ta, Ni-20Nb-5Ta, Ni-15Nb-10Ta powders, indicating that the mechanical alloying was achieved. (AU)

• Processo FAPESP: 01/07025-1 - Estudo sobre a produção de pós via moagem de alta energia de ligas do sistema Ti-Si-B
• Beneficiário: Alfeu Saraiva Ramos
• Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores