Dias, Mateus B. S.
;
Bormio-Nunes, Cristina
;
Pacheco, Clara Johanna
;
Machado, Vagner de Oliveira
;
Hubert, Olivier
Número total de Autores: 5
|
| Tipo de documento: | Artigo Científico |
| Fonte: | Smart Materials and Structures; v. 24, n. 10, p. 7-pg., 2015-10-01. |
| Resumo | |
Textural analysis of a Fe-Al-B alloy obtained by directional solidification indicates an average direction of solidification of < 310 >, close to < 100 >. The magnetomechanical behavior is characterized by the sensing and actuation sensitivities d(33) = dB/d sigma vertical bar(II) and d(33)* = d lambda l/dH vertical bar(sigma), respectively. The Fe2B phase does not act as a pinning center against domain wall movement, proved by the achieved d(33) congruent to d(33)* reversible thermodynamic condition. This phase also does not degrade the saturation magnetization of the alloy, because it has a high saturation magnetization of 1.5 T. Relatively high sensitivities of 13 kA m(-1) MPa-1 were obtained for very low fields of similar to 4 kA m(-1), the same magnitude as that obtained in rare earth based materials, but for much lower fields. The good formability and machining properties of the Fe-Al-B alloy are also of benefit compared to rare earth based materials. (AU) | |
| Processo FAPESP: | 11/21258-0 - Construção de um sensor de força usando a liga Fe-Ga e a liga Fe-Al dopada com boro |
| Beneficiário: | Cristina Bormio Nunes |
| Modalidade de apoio: | Auxílio à Pesquisa - Regular |