Ceria-based/Ni cermets were studied as the catalytic layer deposited onto the standard yttria-stabilized zirconia/Ni anode for direct ethanol solid oxide fuel cells. The influence of the dopant on both Zr- and Nb-doped (10 mol%) ceria and pure ceria was investigated on the properties of cermets with Ni similar to 15% volume fraction. Electrolyte-supported fuel cells with ceria-based/Ni catalytic layer were tested for similar to 100 hours under (dry) ethanol. Fuel cells using the different ceria/Ni cermets showed excellent stability on ethanol, irrespectively of the different properties of the ceramic phase of the catalytic layer. Fuel cells results confirmed that the studied ceria-based cermets are stable catalysts towards ethanol steam reforming. (AU) | |
| Processo FAPESP: | 14/50279-4 - Brasil Research Centre for Gas Innovation |
| Beneficiário: | Julio Romano Meneghini |
| Modalidade de apoio: | Auxílio à Pesquisa - Programa Centros de Pesquisa Aplicada |
| Processo FAPESP: | 14/09087-4 - Estudos sobre o uso do bioetanol em células a combustível do tipo PEMFC e SOFC |
| Beneficiário: | Marcelo Linardi |
| Modalidade de apoio: | Auxílio à Pesquisa - Temático |
| Processo FAPESP: | 13/26961-7 - Desenvolvimento de ânodos de células a combustível de óxidos sólidos operando diretamente com combustíveis renováveis |
| Beneficiário: | Fabio Coral Fonseca |
| Modalidade de apoio: | Auxílio à Pesquisa - Regular |