Structural and properties of nanocrystalline WO3/TiO2-based humidity sensors elements prepared by high energy activation

Texto completo
Autor(es):
Rocha, K. O. [1] ; Zanetti, S. M. [1, 2]
Número total de Autores: 2
Afiliação do(s) autor(es):
[1] SENCER Sensores Ceram Ltda, BR-13566445 Sao Carlos, SP - Brazil
[2] UNESP, INCTMN Inst Quim, BR-14800900 Araraquara, SP - Brazil
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: SENSORS AND ACTUATORS B-CHEMICAL; v. 157, n. 2, p. 654-661, OCT 20 2011.
Citações Web of Science: 18
Resumo

Nanocrystalline WO(3)/TiO(2)-based powders have been prepared by the high energy activation method with WO(3) concentration ranging from 1 to 10 molt The samples were thermal treated in a microwave oven at 600 C for 20 min and their structural and micro-structural characteristics were evaluated by X-ray diffraction, Raman spectroscopy, EXAFS measurements at the Ti K-edge, and transmission electron microscopy. Nitrogen adsorption isotherms and H(2) Temperature Programmed Reduction were also carried out for physical characterization. The crystallite and particle mean sizes ranged from 30 to 40 nm and from 100 to 190 nm, respectively. Good sensor response was obtained for samples with at least 5 mol% WO(3) activated for at least 80 min. Ceramics heat-treated in microwave oven for 20 min have shown similar sensor response as those prepared in conventional oven for 120 min, which is highly cost effective. These results indicate that WO(3)/TiO(2) ceramics can be used as a humidity sensor element. (C) 2011 Elsevier B.V. All rights reserved. (AU)