Autor(es)

Paschoal, Joao Paulo de Oliveira ; Dantas, Andre Victor Rodrigues ; Fernandes, Fernando Almeida da Silva ; Fals, Hipolito Domingo Carvajal ; Thomas, Vinoy ; Zoqui, Eugenio Jose

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS SCIENCE AND TECHNOLOGY; v. N/A, p. 16-pg., 2025-04-22.

Resumo

Traditional 7075 aluminum alloys are difficult to cast due to low viscosity and high shrinkage. This study addresses these challenges by forming TiAl3 particles in situ, which enhance viscosity, reduce porosity, and prevent shrinkage cracks. The method involves adding a titanium master alloy to molten 7075 and using mechanical stirring to induce TiAl3 formation. This improves processability, making the alloy suitable for high-pressure die casting (HPDC) in the aerospace and automotive industries. Microstructural analysis confirms that uniformly distributed TiAl3 particles refine grains and enhance stability. The study employs microscopy, X-ray diffraction, thermodynamic simulations, and mechanical testing to validate structural properties, advancing 7075 alloy processing for large-scale applications in semisolid techniques. (AU)

• Processo FAPESP: 22/05050-5 - Reofundição de Novas Ligas Alumínio-Titânio
• Beneficiário: Eugênio José Zoqui
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 24/06996-5 - Processamento de Ligas Semissólidas em Matriz Funcional
• Beneficiário: Eugênio José Zoqui
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 23/09182-6 - Processamento no estado semissólido de novos materiais Al-Ti-(Zn-Cu-Mg). Propriedades mecânicas, resistência ao desgaste e à corrosão
• Beneficiário: Eugênio José Zoqui
• Modalidade de apoio: Auxílio à Pesquisa - Pesquisador Visitante - Internacional
• Processo FAPESP: 18/11802-4 - Propriedades Mecânicas de Novas Ligas Al-Si-(Zn-Cu-Mg) Reofundidas e Tixoconformadas
• Beneficiário: Eugênio José Zoqui
• Modalidade de apoio: Auxílio à Pesquisa - Regular