Effect of Ta2O5 addition on the texture of the Y123 superconductor

Autor(es)

Oliveira, C. J. V. ; Bortolozo, A. D. ; Ferreira, B. ; Santos, C. A. M. dos ; Machado, A. J. S. ^[5]

• Tipo de documento: Artigo Científico
• Fonte: PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS; v. 422, n. 3/4, p. 83-87, June 2005.
• Área do conhecimento: Engenharias - Engenharia de Materiais e Metalúrgica
• Assunto(s): Materiais não metálicos Análise térmica Difração por raios X Supercondutividade Microscopia eletrônica de varredura

Resumo

In this work we present a systematic study of the Ta influence on the texture of Y123 superconducting phase. The differential thermal analysis (DTA) results show a systematic decreasing of the peritectic temperature, from 1020 ºC for Y123 without Ta doping to approximately 950 ºC for Y 0.92Ta0.08Ba2Cu3Oy composition. The excellent texture reached by samples is confirmed through X-ray diffraction (TETA/2TETA) which reveals only (0 0 l) reflections, consistent with the rocking curve measurement in which FWHM 0.2º. The microstructures observed by scanning electron microscopy (SEM) indicate segregation of an additional phase. The energy dispersive spectrometry (EDS) revealed that this phase has the Y0.5Ta0.5BaO3 stoichiometry. (AU)

• Processo FAPESP: 02/04558-1 - Estudo da texturizacao do supercondutor yba2cu3o7-y dopado com ta.
• Beneficiário: Ausdinir Danilo Bortolozo
• Modalidade de apoio: Bolsas no Brasil - Iniciação Científica
• Processo FAPESP: 02/09997-3 - Influencia da dopagem de ta na texturizacao do supercondutor yabaecu307.
• Beneficiário: Antonio Jefferson da Silva Machado
• Modalidade de apoio: Auxílio à Pesquisa - Regular