Microstructural and Fractographic Characterization of a Thermally Embrittled Nuclear Grade Steel: Part II - Quenching and Tempering

Texto completo
Autor(es):
José R. Tarpani ; Maria H.P. Braz ; Waldek W. Bose Filho ; Dirceu Spinelli
Número total de Autores: 4
Tipo de documento: Artigo Científico
Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 5, n. 3, p. 365-371, Set. 2002.
Resumo

A nuclear reactor pressure vessel steel was submitted to different quenching and tempering heat treatments aimed at simulating neutron irradiation damage. The obtained microstructures were mechanically tested and submitted to metallographic and fractographic survey. The relevant microstructural and fractographic aspects were employed in the interpretation of the mechanical performance of the thermally embrittled microstructures. A well defined correlation was determined between the elastic-plastic fracture toughness parameter J-integral and the Charpy impact energy, which was achieved for some of the Q&T microstructures. (AU)

Processo FAPESP: 97/05652-1 - Aplicação da mecânica da fratura em simulações de danos por irradiação de vasos nucleares internamente pressurizados
Beneficiário:José Ricardo Tarpani
Linha de fomento: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 99/09431-5 - Propriedades de tenacidade ao impacto instrumentado Charpy de um aço de grau nuclear
Beneficiário:Dirceu Spinelli
Linha de fomento: Auxílio à Pesquisa - Regular