An evaluation of the tribological characteristics of DLC films grown on Inconel Alloy 718 using the Active Screen Plasma technique in a Pulsed-DC PECVD system

Autor(es)

Ramirez, Marco A. R. ^[1] ; Silva, Patricia C. ^[1] ; Corat, Evaldo J. ^[1] ; Trava-Airoldi, Vladimir J. ^[1]

Afiliação do(s) autor(es)

^[1] INPE, LAS, BR-12227010 Sao Jose Dos Campos, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: SURFACE & COATINGS TECHNOLOGY; v. 284, p. 235-239, DEC 25 2015.
• Citações Web of Science: 10

Resumo

Tribology properties of Diamond-Like Carbon (DLC) films are important for the petroleum industry because of their low friction coefficient, hardness, good wear resistance, and corrosion. In this study, the DLC films were deposited on Inconel Alloy 718, using the Active Screen Plasma (ASP) technique in a Pulsed DC-PECVD system. Plasma carbonitriding was used as a pretreatment followed by the deposition of an amorphous silicon interlayer to increase adhesion and improve the tribological performance of the DLC coatings; everything described above was performed in a single continuous process of deposition. This paper analyzes the tribological behavior of the DLC films. The layers were observed with SEM and Raman spectroscopy. The tribological behavior was analyzed by linearly reciprocating wear tests at room temperature and at 150 degrees C. Adhesion was tested according to the VDI3198 standard based on a Rockwell C indentation and scratch test. The coatings registered a hardness of 20 GPa, showing better wear resistance and elevated adhesion, than the uncoated substrate. (C) 2015 Elsevier B.V. All rights reserved. (AU)

• Processo FAPESP: 13/22458-9 - Deposição de filmes de DLC (Diamond Like Carbon) sobre aços para ferramentas AISI D2 e AISI H13 para aplicações industriais em geral
• Beneficiário: Marco Antonio Ramirez Ramos
• Modalidade de apoio: Bolsas no Brasil - Doutorado