Functionalization of Multi-Walled Carbon Nanotube and Mechanical Property of Epoxy-Based Nanocomposite

Texto completo
Autor(es):
Wesley Francisco [1] ; Filipe Vargas Ferreira [2] ; Eduardo Vargas Ferreira [3] ; Luciana de Simone Cividanes [4] ; Aparecido dos Reis Coutinho [5] ; Gilmar Patrocínio Thim [6]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Instituto Tecnológico de Aeronáutica. Departamento de Ciência e Tecnologia Aeroespacial. Divisão de Ciências Fundamentais - Brasil
[2] Instituto Tecnológico de Aeronáutica. Departamento de Ciência e Tecnologia Aeroespacial. Divisão de Ciências Fundamentais - Brasil
[3] Universidade Federal de Juiz de Fora. Departamento de Estatística - Brasil
[4] Instituto Tecnológico de Aeronáutica. Departamento de Ciência e Tecnologia Aeroespacial. Divisão de Ciências Fundamentais - Brasil
[5] Universidade Metodista de Piracicaba. Laboratório de Materiais Carbonosos - Brasil
[6] Instituto Tecnológico de Aeronáutica. Departamento de Ciência e Tecnologia Aeroespacial. Divisão de Ciências Fundamentais - Brasil
Número total de Afiliações: 6
Tipo de documento: Artigo Científico
Fonte: J. Aerosp. Technol. Manag.; v. 7, n. 3, p. 289-293, 2015-09-00.
Resumo

ABSTRACT: The focus of this study is to evaluate the effect of carboxyl and amino functionalization of multiwalled carbon nanotubes on the mechanical property of the epoxy resin filled with modified carbon nanotubes. The carbon nanotubes were treated with sulfuric and nitric acids and also with hexamethylenediamine. The presence of acid and amine chemical groups on the carbon nanotube surface was confirmed by X-ray photoelectron spectroscopy. The composites were produced with epoxy resin and modified carbon nanotubes. Vickers hardness tests were carried out on the composites and neat resin. The results showed an increase of hardness in the composite prepared with functionalized carbon nanotubes. This phenomenon is due to the fact that the chemical interaction between modified carbon nanotube and epoxy resin is much stronger than between pristine carbon nanotube and epoxy resin. This stronger interaction is related to the presence of functionalized carbon nanotubes. (AU)

Processo FAPESP: 13/23042-0 - Reação de sonodegradação catalisada pelo nanocompósito grafeno/TiO2
Beneficiário:Gilmar Patrocínio Thim
Modalidade de apoio: Auxílio à Pesquisa - Regular
Processo FAPESP: 13/20218-0 - Nanocompósito CNT/PEAD: efeito da funcionalização com alcanos
Beneficiário:Filipe Vargas Ferreira
Modalidade de apoio: Bolsas no Brasil - Mestrado